Abstract:Cellulose, oxidized-�bers, and oxidized-nanocellulose were isolated from sponge-gourd �bers (Luffa cylindrica). Isolated materials showed different morphology (shape and size), chemical, crystalline properties, and removal e�ciency against methylene blue (MB) and lead ions (Pb 2+ ). The cellulosic materials showed high e�ciency in removing MB more than Pb 2+ . So, different luffa forms/hydroxyapatite (HAp) composites were prepared and used as adsorbents for removal of both MB and Pb 2+ from aqueous solutions. The effect of sorbent type, contact time, and initial MB and Pb 2+ concentrations were studied. HAp was successfully synthesized on the surface of luffa with an average length of 40–56 nm and width of 14–19 nm. Kinetic and adsorption studies of MB and Pb 2+ ions were well �tted with the pseudo-second-order model and Langmuir model. The maximum adsorption capacity of MB was 25.2 mg/g, 30.8 mg/g, and 36.2 mg/g for oxidized-�bers/HAp, oxidized-�bers, and cellulose, respectively, and for Pb 2+ was 625 mg/g, 714 mg/g, and 714.5 mg/g for oxidized-�bers/HAp, oxidized-nanocellulose/HAp, and cellulose/HAp, respectively. Also, more than 85% of MB (25 mg/L) and 95% of lead (500 mg/L) were removed within the �rst 5 min. Oxidize-�bers/HAp composite showed effective adsorption with both MB and Pb 2+ in a very short time. (S3), oxidized-�bers/HAp (S4), cellulose/HAp (S5), oxidized-nanocellulose/HAp (S6). Two representative contaminants, methyl and lead (Pb +2 ) were used in this study. Precisely, a 0.4 g of the prepared sorbents was added to 100 mL of 25 mg/L methylene blue or 100 mg/L lead ions solution separately. The mixtures were shaken for 120 minutes and �ltered. Then, the remaining concentrations of were spectrophotometer Varian, England) at wavelength 633 while the remaining Pb +2 ions concentrations were determined by the absorption The removal e�ciency (R%) sorbents was calculated using the following equation

Preparation and characterization of multifunctional sponge-gourd �bers (Luffa cylindrica)/ hydroxyapatite composites for removal of lead and methylene blue