Abstract:Laser remelting (LR) is often used during selective laser melting (SLM) processes to improve the densification degree and top surface quality of the products. However, researches regarding its effects on side surface quality, residual stress, microstructure, and mechanical property are still quite lacking. The influence of the repeated usage of LR on a solidified layer is also not very clear. To address these issues, LR treatments with the cyclic numbers of 1-3 on every solidified layer have been employed during the SLM processes of a Ti-5Al-2.5Sn alloy in this study and their influences on deposition quality, residual stress, microstructure, and mechanical property were researched. The results first indicated that although the improvement in top surface quality and densification degree would be more and more notable with the increase of LR cycles, the side surface quality could not be improved through all the LR treatments. Then, it was shown by the hole-drilling tests on the surface centers of several 15 x 15 x 3 mm(3) thin-plate specimens that when 1 cycle of LR was conducted on every solidified layer, the principal residual stress at the hole bottom of the SLM sample could be far beyond that of the non-treated one. In contrast, when 2 or 3 cycles of LR were conducted, the measured principal residual stresses could be reduced to lower than that of the non-treated ones. It was also proved that unlike the non-treated sample which presented a martensite-dominated microstructure with a very weak texture, all the LR-treated samples exhibited two kinds of preferential orientations. Finally, tensile properties of the stress-relieved samples were tested and it was seen that under the combined influence of the densification and the microstructure factors, the elongations of the LR-treated samples became slightly higher than that of the non-treated one whereas the tensile strengths were nearly identical. In summary, this paper demonstrates that there is still limitation in using LR as an auxiliary process of the SLM production of titanium products. The possible increase in residual stress and the formation of strong textures should be particularly considered.

Optimized Laser Surface Remelting of 3D-Printed Ti6Al4V Manufactured Through Electron Beam Melting

Experimental study on parameters optimization of selective laser melting 316L stainless steel based on response surface methodology

Effect of Surface Modifications on Surface Roughness of Ti6Al4V Alloy Manufactured by 3D Printing, Casting, and Wrought

Parameter optimization of selective laser melting fabricated titanium alloy using skin-core and triple contour scanning strategy

Study on Laser Polishing of Ti6Al4V Fabricated by Selective Laser Melting

Surface roughness improvement of Ti-6Al-4V alloy overhang structures via process optimization for laser-powder bed fusion

Surface Roughness Improvement by Sliding Friction Burnishing of Parts Produced by Selective Laser Melting of Ti6Al4V Titanium Alloy

Two-step laser based surface treatments of laser metal deposition manufactured Ti6Al4V components

Enhancing the corrosion properties and microhardness of titanium alloy by laser surface remelting

Laser polishing of 3D printed mesoscale components

Residual stress reduction in Ti-6Al-4V parts fabricated by laser-foil-printing process

Effects of machining surface and laser beam scanning strategy on machinability of selective laser melted Ti6Al4V alloy in milling

Effect of Laser Remelting on Deposition Quality, Residual Stress, Microstructure, and Mechanical Property of Selective Laser Melting Processed Ti-5Al-2.5Sn Alloy

Superhydrophobic Surface of Ti6Al4V using Direct Nanosecond Laser Texturing

The effect of laser surface re-melting on the surface roughness and micro-hardness of selective laser melting (SLM) fabricated Ti-6Al-4V samples

Investigation of Scanning Strategies and Laser Remelting Effects on Top Surface Deformation of Additively Manufactured IN 625

Effect of Process Parameters on the Mechanical Behavior of Ti6Al4V Alloys Fabricated by Laser Powder Bed Fusion Method

Influence of Laser Parameters and Ti Content on the Surface Morphology of L-PBF Fabricated Titania

Effects of laser polishing on surface morphology and mechanical properties of additive manufactured TiAl components

Melt Pool characteristics on surface roughness and printability of 316L stainless steel in laser powder bed fusion

Surface characteristics of laser polished Ti-6Al-4V parts produced by electron beam melting additive manufacturing process