Abstract:Nickel-based superalloy IN713C produced through investment casting route is widely used for turbocharger turbine wheels in the automotive industry. The produced microstructure and microtexture are not homogeneous across the turbine component due to geometrical factors and localised cooling rate during the casting process, which give rise to inhomogeneous deformation during service. In the present paper, two kinds of in-house fatigue tests, Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF), were conducted at 600 °C in attempt to simulate the actual fatigue conditions experienced by turbine wheels in turbocharger. From Geometrically Necessary Dislocation (GND) distributions and strain analyses, it is concluded that microstructure heterogeneity such as carbide precipitates distribution within dendritic structure network determine the failure micromechanics during LCF tests. In the early stage of LCF loading, crack principally initiated within near surface carbides that have been oxidised during high temperature exposure. The higher GND density at the tip of carbide precipitates due to oxidation volume expansion are found to facilitate easy cracks initiation and propagation. Moreover, the cluster-like carbides network and its distribution can accelerate oxidation process and crack growth effectively. Furthermore, in the later stage of crack propagation during LCF, the weak interdendrite areas rotate to accommodate increased strain leading to faster cracks propagation and hence final catastrophic failure. Serial section technique for 3-D visualisation was employed to investigate the crystallographic grain orientation correlation with fracture mechanics during HCF loading. It appears that the microtexure and grain orientations are more critical than the alloy microstructure in an area with a relatively uniform carbides distribution and weak dendrite structure where HCF failure occurred. Based on the slip trace analysis, it was found that most faceting occurred in Goss grains (<110>//LD) and on slip system with the highest Schmid factor. It is concluded that cracks were initiated on planes with high Schmid factors and assisted by the presence of porosity.

Interaction and superposition of creep damage and high-cycle fatigue of coarse-grained nickel-base alloy 247

Characterisation of the creep cavitation process on grain boundaries in a polycrystalline nickel-base alloy 247

Creep Behavior and Deformation Mechanism of a Third-Generation Single Crystal Ni-Based Superalloy at 980 °C

High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

The creep-fatigue behavior of a nickel-based superalloy: Experiments study and cyclic plastic analysis

Creep-fatigue damage mechanisms and life prediction based on crystal plasticity combined with grain boundary cavity model in a nickel-based superalloy at 650°C

The Effects of Inhomogeneous Microstructure and Loading Waveform on Creep-Fatigue Behaviour in a Forged and Precipitation Hardened Nickel-Based Superalloy

Creep-fatigue life prediction in nickel-based superalloy GH4169 based on microstructural damage quantification with the help of electron backscatter diffraction

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

Crystal plasticity analysis of fatigue-creep behavior at cooling holes in single crystal Nickel based gas turbine blade components

Creep-fatigue Life Prediction and Interaction Diagram in Nickel-Based GH4169 Superalloy at 650 °C Based on Cycle-by-cycle Concept

The Effects of Microstructure and Microtexture Generated During Solidification on Deformation Micromechanism in IN713C Nickel-Based Superalloy

Stress-strain Histories in Coatings on Single Crystal Specimens of a Turbine Blade Alloy

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Coating-assisted deterioration mechanism of creep resistance at a nickel-based single-crystal superalloy

Experimental investigation on creep strengthening phenomenon of a Ni-based single crystal superalloy under cyclic loading and unloading conditions

A study of high cycle fatigue life and its correlation with microstructural parameters in IN713C nickel-based superalloy

Couple effects of temperature and fatigue, creep-fatigue interaction and thermo-mechanical loading conditions on crack growth rate of nickel-based alloy

Failure mechanism of single-crystal superalloy NiAlReRu components with film cooling holes under the coupling high-speed rotating and high temperature condition

Fatigue Strength and Life Prediction of a MAR-M247 Nickel-Base Superalloy Gas Turbine Blade with Multiple Carbide Inclusions