Stress-strain Histories in Coatings on Single Crystal Specimens of a Turbine Blade Alloy

EP BUSSO,FA MCCLINTOCK
DOI: https://doi.org/10.1016/0020-7683(88)90009-1
IF: 3.667
1988-01-01
International Journal of Solids and Structures
Abstract:The stress-strain response of an electron beam, physical vapor deposited (EB-PVD) NiCoCrAlY overlay coating applied to a single crystal nickel base superalloy (CMSX-3) is studied by subjecting stepped-disk fatigue specimens to thermal cycles with different rates of heating (from 520 to 1090†C in 4.5, 6, and 20 s) and cooling (to 520°C in 7 and 15 s). Rate-dependent material anisotropy is modelled using a creep (or flow) potential for a cubic crystal and the associated flow rule. An anisotropic creep finite element analysis of the substrate reveals that continued cycling does not affect the strain ranges, which play a role in coating degradation. However, continued cycling does produce an increase of the peak tensile stresses (from 13 MPa for the first cycle to about 250 MPa at the 6000th cycle for 4.5 s heating history). Most of this transition occurs before the 500th cycle. As a consequence of these tensile stresses, crack propagation rates into the substrate are expected to be more severe than the predictions from a thermo-elastic analysis. However, the conventional thermo-elastic analysis is very accurate at estimating the strain ranges. For the coating, an isotropic creep finite element analysis shows that the mechanical strain range (Δεe + Δεc) and tensile peak stresses responsible for crack initiation and crack growth, with 0.52% strain range in the substrate, are 0.83% and 460 MPa for the 4.5 s heating cycle, due in large part to the thermal expansion mismatch between the coating and substrate.
What problem does this paper attempt to address?