Abstract:Nano zero-valent iron (Fe0, nZVI) has been extensively utilized in the treatment of dyed wastewater. However, the dispersibility, stability and reusability of nZVI need to be improved for both efficiency and environmental safety. One nZVI modified nanofiber composite membrane was successfully fabricated by electrospinning, and the performances in different catalytic systems were evaluated. The synthesized composite mat was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The loaded nZVI was verified by the change of fiber diameters and the distribution of iron element with/without loading. The composite membrane possessed good recyclability and dispersion property of nZVI with a mean diameter of 114.46 nm. Three Fenton-like oxidation systems (H2O2, Na2S2O8, and NaClO2) were selected and investigated for the degradation of Rhodamine B (RhB) in water using the as-prepared composite as a catalyzer. The degradability relationship of the oxidation systems was NaClO2>Na2S2O8>H2O2 with observed rate constants (Kobs) of 0.3155, 0.0547, and 0.014, respectively. 50 mg L−1 RhB was completely degraded by 1.5 mM NaClO2 in 15min, which is the best compared with the other two systems. The major free radical species (·OH, SO4·- and ClO2·) in the three oxidation systems were identified by electron paramagnetic resonance (EPR) and quenching studies. The degradation capacity could be maintained after five recycles and the leached nZVI from the composite was negligible (<0.55%). For the degradation process, the contribution of dark adsorption (Kads = 1.5489 × 10−3) was much smaller than that of natural-light-derived photocatalysis (Kphoto = 1.5489 × 10−3) with the adsorption capacity of 4.32 mg g−1 and oxidative degradation amounts of 9.46 mg g−1, 10.90 mg g−1 and 12.32 mg g−1 in H2O2, Na2S2O8 and NaClO2 systems, respectively. Our results demonstrated that the synthesized composite membrane demonstrated good catalytic properties with good recyclability and stability, and NaClO2 was the most efficacious system for RhB degradation in water.

Synthesis, magnetic properties, biotoxicity and potential mechanism of modified nano zero-valent iron for decolorization of dye wastewater

Preparation of a novel modified nanoscale zero valent iron particles and its decolorization of methyl orange solution

Preparation of Biomass Activated Carbon Supported Nanoscale Zero-Valent Iron (nzvi) and Its Application in Decolorization of Methyl Orange from Aqueous Solution

Nanoscale zero-valent iron integrated with bioreactor for recalcitrant antimony-Congo red dyeing wastewater treatment

Green Synthesis of Nanoscale Zero-Valent Iron Aggregates for Catalytic Degradation of Textile Dyes

Accelerated Decoloration of Organic Dyes from Wastewater Using Ternary Metal/g-C3N4/ZnO Nanocomposites: An Investigation of Impact of g-C3N4 Concentration and Ni and Mn Doping

Preparation of stabilized nano zero-valent iron particles via a rheological phase reaction method and their use in dye decolourization

Stabilization of nano zero-valent iron by electrospun composite mat with good catalysis and recyclability

Treatment of Dye Wastewater by Zero Valent Iron Composited Organobentonite

Probing the performance and mechanisms of Congo red wastewater decolorization with nanoscale zero-valent iron in the continuing flow reactor

Green Synthesis of Nano-Zero-Valent Iron Using Ricinus Communis Seeds Extract: Characterization and Application in the Treatment of Methylene Blue-Polluted Water

Magnetic nanocomposite microbial extracellular polymeric substances@Fe3O4 supported nZVI for Sb(V) reduction and adsorption under aerobic and anaerobic conditions

Nanoscale zero-valent iron for remediation of toxicants and wastewater treatment

Removal of organic compounds by nanoscale zero-valent iron and its composites

Simultaneous Molybdate (mo(vi)) Recovery and Hazardous Ions Immobilization Via Nanoscale Zerovalent Iron.

Cheap, fast and durable degradation of azo dye wastewater by zero-valent iron structural composites

Nanozinc ferrites @ silica as efficient adsorbent for dye removal from wastewater: synthesis and adsorption studies

Engineered Iron Nanoparticles via Green Routes and Their Applications for Textile Wastewater Treatment

The Application of Modified Hematite for Removal of Carmine Red Dye: Performance and Mechanism

"Synthesis of Zero-Valent Iron Nanoparticles on Polyester Non-Woven Fabric Using Green Chemistry Method for Wastewater Treatment in the Textile Dyeing Industry"

The Synthesis of Metal–Organic-Framework-Based Ternary Nanocomposite for the Adsorption of Organic Dyes from Aqueous Solutions