Abstract:Nano zero-valent iron (Fe0, nZVI) has been extensively utilized in the treatment of dyed wastewater. However, the dispersibility, stability and reusability of nZVI need to be improved for both efficiency and environmental safety. One nZVI modified nanofiber composite membrane was successfully fabricated by electrospinning, and the performances in different catalytic systems were evaluated. The synthesized composite mat was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The loaded nZVI was verified by the change of fiber diameters and the distribution of iron element with/without loading. The composite membrane possessed good recyclability and dispersion property of nZVI with a mean diameter of 114.46 nm. Three Fenton-like oxidation systems (H2O2, Na2S2O8, and NaClO2) were selected and investigated for the degradation of Rhodamine B (RhB) in water using the as-prepared composite as a catalyzer. The degradability relationship of the oxidation systems was NaClO2>Na2S2O8>H2O2 with observed rate constants (Kobs) of 0.3155, 0.0547, and 0.014, respectively. 50 mg L−1 RhB was completely degraded by 1.5 mM NaClO2 in 15min, which is the best compared with the other two systems. The major free radical species (·OH, SO4·- and ClO2·) in the three oxidation systems were identified by electron paramagnetic resonance (EPR) and quenching studies. The degradation capacity could be maintained after five recycles and the leached nZVI from the composite was negligible (<0.55%). For the degradation process, the contribution of dark adsorption (Kads = 1.5489 × 10−3) was much smaller than that of natural-light-derived photocatalysis (Kphoto = 1.5489 × 10−3) with the adsorption capacity of 4.32 mg g−1 and oxidative degradation amounts of 9.46 mg g−1, 10.90 mg g−1 and 12.32 mg g−1 in H2O2, Na2S2O8 and NaClO2 systems, respectively. Our results demonstrated that the synthesized composite membrane demonstrated good catalytic properties with good recyclability and stability, and NaClO2 was the most efficacious system for RhB degradation in water.

Cheap, fast and durable degradation of azo dye wastewater by zero-valent iron structural composites

Sustainable and cost-effective metastable white cast iron powder for the degradation of textile dyes

Tailoring the properties of a zero-valent iron-based composite by mechanochemistry for nitrophenols degradation in wastewaters

Intrinsic Fast Kinetics on the Degradation of Azo Dye by Iron in Alkaline Condition

Zero valent iron (ZVI) mediated Fenton degradation of industrial wastewater: Treatment performance and characterization of final composites

Synthesis, magnetic properties, biotoxicity and potential mechanism of modified nano zero-valent iron for decolorization of dye wastewater

Designing hierarchically porous zero-valent iron via 3D printing to degrade organic pollutants by activating peroxymonosulfate using high-valent iron-oxo species

Reducing Degradation Of Azo Dye By Zero-Valent Iron In Aqueous Solution

Degradation of azo dye active brilliant red X-3B by composite ferrate solution

Effective Removal of Orange II Dye by Porous Fe-base Amorphous/cu Bimetallic Composite

Degradation of azo dye C.I. Reactive Black 5 by composite ferrate solution

Porous composite architecture bestows Fe-based glassy alloy with high and ultra-durable degradation activity in decomposing azo dye.

Stabilization of nano zero-valent iron by electrospun composite mat with good catalysis and recyclability

Influence of iron content in Fe-based amorphous alloy catalysts on degradation of azo dyes by fenton-like process

A Zn-Ca-Based Metallic Glass Composite Material for Rapid Degradation of Azo Dyes

Synergistic effect of extracellular polymeric substances and carbon layer on electron utilization of Fe@C during anaerobic treatment of refractory wastewater

A Feasible Approach for Azo Dye Degradation Using Natural Magnetite in Heterogeneous Fenton Oxidation

Effects of an Electric Field and Zero Valent Iron on Anaerobic Treatment of Azo Dye Wastewater and Microbial Community Structures.

Treatment of Dye Wastewater by Zero Valent Iron Composited Organobentonite

Enhancing the acid orange dye degradation efficiency of Mg-based glassy alloys with introducing porous structure and zinc oxide

Mesoporous zinc silicate composites derived from iron ore tailings for highly efficient dye removal: Structure and morphology evolution