Abstract:The HIsmelt smelting reduction process is an efficient direct reduction process for smelting vanadium titanomagnetite ores. About 80% vanadium is enriched in the reduction slag, however, due to the low vanadium and high calcium content in reduction slag, it is difficult to extract the vanadium economically. In this study, a process featuring in situ sodium salt oxidation and alkali leaching was proposed to extract vanadium. Efficiently in situ sodium salt oxidation process was achieved by adding sodium salts to the molten reduction slag, which was freshly discharged from HIsmelt SRV furnace. The equilibrium phases of the slag after the introduction of sodium salts were calculated and simulated by thermodynamic software. The vanadium containing phase was detected used XRD and SEM–EDS analysis. For the leaching process, the effects of NaOH concentration, temperature, particle size, liquid–solid ratio (mass ratio), and stirring speed were investigated. The optimal reaction conditions were confirmed to be the mass fraction of Na2CO3 of 10 wt%, the oxygen pressure of 0.5 MPa, oxygenation time of 10 min, the temperature of 90 °C, the liquid–solid ratio of 4:1, the stirring speed of 500 rpm, the mass concentration of NaOH of 35 wt%, and the reaction time of 240 min. The final vanadium extraction rate reached 85.5% under optimal conditions. Kinetic analysis indicated that the internal diffusion was the controlling step of the leaching reaction, and the apparent reaction activation energy value was calculated to be 18.34 kJ/mol. This method is expected provide an attractive approach to extract vanadium from HIsmelt reduction slag with low energy consumption.Graphical Abstract

Distribution behavior of vanadium and titanium between hot metal and high titanium slag relevant to HIsmelt smelting condition

Effect of Smelting Time on Vanadium and Titanium Distribution Behavior and Slag Viscosity in HIsmelt

Analysing the HIsmelt process for smelting vanadium–titanium magnetite

Effect of Basicity and MgO/Al2O3 Ratio on Viscosity and Crystallization Behavior of HIsmelt Titanium‐Containing Slag

A thermodynamic model for predicting activity of CaO–SiO2–Al2O3–MgO–TiO2–V2O3–FeO slags during electric furnace smelting process

Performance calculation of slag from vanadium titano-magnetite by full oxygen bath smelting process

Enrichment and reconfiguration of titanium-bearing phase in vortex smelting reduction process of vanadium–titanium magnetite

Study on the High-temperature Properties of High-titania Slags produced with Cr-bearing Vanadia-titania Magnetite Smelting in Blast Furnace

High-Efficiency Smelting Separation of Vanadium–Titanium Magnetite by Electrothermal Smelting: Parameter Optimization and Element Enrichment Mechanism

Fusion Separation of Vanadium-Titanium Magnetite and Enrichment Test of Ti Element in Slag

Softening–Melting Properties and Slag Evolution of Vanadium Titano-Magnetite Sinter in Hydrogen-Rich Gases

Phase transformation and slag evolution of vanadium–titanium magnetite pellets during softening–melting process

Study of the High Temperature Metallurgical Properties of On-Site Samples with Vanadium–Titanium Magnetite

Titanium Impurity Control in V-Bearing Pig Iron Prepared via the Sodium Smelting of Vanadium–Titanium Magnetite

Softening-melting Properties of High-chromium Vanadium–titanium Magnetite Pellets with Different Basicity

Smelting Reduction Characteristics and Mechanism of Vanadium–Titanium Magnetite Carbon-Bearing Pellet

Sulphide capacity of CaO-SiO2-Al2O3-MgO-TiO2-FetO slag with high titanium and high FeO content based on HIsmelt process

A Method to Extract Vanadium from HIsmelt Reduction Slag: In Situ Sodium Salt Oxidation and Alkali Leaching

Investigation of Basicity on Compressive Strength and Oxidation Induration Mechanism of Vanadium–Titanium Magnetite Pellets

Thermodynamic design of electroslag remelting slag for high titanium and low aluminium stainless steel based on IMCT

Numerical Simulation of Vanadium–Titanium Blast Furnace under Different Smelting Intensities