Room temperature ferromagnetism in chemically synthesized ZnO rods

Shalendra Kumar,Y. J. Kim,B. H. Koo,S. Gautam,K. H. Chae,Ravi Kumar,C. G. Lee

DOI: https://doi.org/10.1016/j.matlet.2008.09.057

2009-11-22

Abstract:We report structural and magnetic properties of pure ZnO rods using X-ray diffraction (XRD), magnetization hysteresis (M-H) loop and near edge x-ray fine structure spectroscopy (NEXAFS) study at O K edge. Sample of ZnO was prepared by co-precipitation method. XRD and selective area electron diffraction measurements infer that ZnO rods exhibit a single phase polycrystalline nature with wurtzite lattice. Field emission transmission electron microscopy, field emission scanning electron microscopy micrographs infers that ZnO have rod type microstructures with dimension 200 nm in diameter and 550 nm in length. M-H loop studies performed at room temperature display room temperature ferromagnetism in ZnO rods. NEXAFS study reflects absence of the oxygen vacancies in pure ZnO rods.

Materials Science,Mesoscale and Nanoscale Physics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: achieving room - temperature ferromagnetism (RTFM) in pure zinc oxide (ZnO) nanorods. Specifically, the authors prepared pure ZnO nanorods by chemical synthesis methods and conducted a detailed study of their structures and magnetism to verify whether these materials can exhibit ferromagnetism at room temperature. The solution to this problem is of great significance for the development of new spintronic devices, because room - temperature ferromagnetic semiconductors can be used in applications such as non - volatile memories and quantum computing.

### Main research contents:
1. **Material preparation**: Pure ZnO nanorods were synthesized by the co - precipitation method.
2. **Structural characterization**:
- X - ray diffraction (XRD) and selected - area electron diffraction (SAED) were used to confirm that the ZnO nanorods have a single - phase polycrystalline structure with a wurtzite lattice.
- Through field - emission scanning electron microscopy (FESEM) and transmission electron microscopy (FETEM), it was observed that the size of the ZnO nanorods is approximately 200 nm in diameter and 550 nm in length.
3. **Magnetic measurement**: Hysteresis loop (M - H) measurements were carried out at room temperature, and the results showed that the ZnO nanorods have room - temperature ferromagnetism, with a saturation magnetization of \(2.0\times 10^{-3}\, \text{emu/g}\) and a coercive force of 102 Oe.
4. **Defect analysis**: Through near - edge X - ray absorption fine - structure (NEXAFS) spectroscopy research, it was found that there are no oxygen vacancies in pure ZnO nanorods, suggesting that ferromagnetism may originate from spin polarization induced by zinc vacancies (Zn vacancies).

### Key conclusions:
- Pure ZnO nanorods exhibit ferromagnetism at room temperature, which is consistent with previous theoretical and experimental results, that is, ferromagnetism may be caused by zinc vacancies, rather than oxygen vacancies or other defects.

### Formula examples:
- Saturation magnetization: \[M_s = 2.0\times 10^{-3}\, \text{emu/g}\]
- Coercive force: \[H_c = 102\, \text{Oe}\]

Through these studies, the authors have provided new insights into understanding the origin of ferromagnetism in pure ZnO materials and laid the foundation for further exploring its applications in spintronics.