Effect of chitosan-epoxy ratio in bio-based adhesive on physical and mechanical properties of medium density fiberboards from mixed hardwood fibers

Alireza Ashori,Anton Kuzmin
DOI: https://doi.org/10.1038/s41598-024-55796-x
IF: 4.6
2024-03-02
Scientific Reports
Abstract:Chitosan and bio-based epoxy resins have emerged as promising formaldehyde-free replacements for traditional urea–formaldehyde (UF) adhesives in engineered wood products. This study evaluated five chitosan-to-epoxy weight ratios (3:1, 2:1, 1:1, 1:2, 1:3) as adhesives for hot-pressing medium density fiberboards (MDF) using mixed hardwood fibers. Increasing the epoxy ratio reduced viscosity and gel time, facilitating spraying and fast curing. The density of the formulated MDFs increased with higher epoxy ratios, ranging from 679 kg/m 3 for the 3:1 ratio to 701 kg/m 3 for the 1:3 formulation, meeting the 500–900 kg/m 3 density range specified in EN 323. The 1:3 epoxy-rich formulation enhanced modulus of rupture (MOR) to 31 MPa and modulus of elasticity (MOE) to 2392 MPa, exceeding the minimum requirements of 16 MPa and 1500 MPa set out in EN 310 and EN 316, respectively. Dimensional stability peaked at 5% thickness swelling for the 1:3 formulation after 24 h water soaking, fulfilling the < 25% requirement per EN 316. Internal bond strength reached a maximum of 0.98 MPa for the 3:1 chitosan-rich formulation, satisfying the 0.40 MPa minimum per EN 319. One-way ANOVA tests showed the adhesive ratio had a significant effect on mechanical properties and dimensional stability at 95–99% confidence levels. Duncan's multiple range test revealed the 1:3 ratio boards exhibited statistically significant improvements compared to untreated group. Overall, tailoring the ratios achieved well-balanced properties for MOR, MOE, and dimensional stability, demonstrating potential to replace UF resins.
multidisciplinary sciences
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to develop an optimized chitosan - epoxy resin - based bio - adhesive to replace the traditional urea - formaldehyde resin (UF) for the production of medium - density fiberboard (MDF). Specifically, the research aims to find the optimal ratio by adjusting the ratio of chitosan to epoxy resin, thereby improving the physical and mechanical properties of MDF and ensuring its environmental - friendliness and formaldehyde - free release characteristics. ### Main Problems and Objectives 1. **Reduce formaldehyde release**: - Traditional urea - formaldehyde resin is widely used in wood composites, but because it releases formaldehyde, it poses a threat to indoor air quality and human health. Therefore, finding a formaldehyde - free substitute has become an urgent need. 2. **Improve the physical and mechanical properties of MDF**: - The research evaluates the influence of different ratios (3:1, 2:1, 1:1, 1:2, 1:3) of chitosan to epoxy resin on the density, modulus (such as bending strength MOR and elastic modulus MOE), internal bond strength (IBS), thickness swelling rate (TS), and water absorption rate (WA) of MDF. 3. **Optimize the performance of the adhesive**: - By systematically adjusting the ratio of chitosan to epoxy resin, the research finds that increasing the proportion of epoxy resin can reduce viscosity and gel time, thereby improving sprayability and rapid curing performance. In addition, the influence of different ratios on MDF density and other key performance parameters is also explored. ### Experimental Results and Conclusions - **Density**: As the proportion of epoxy resin increases, the density of MDF increases from 679 kg/m³ (3:1 ratio) to 701 kg/m³ (1:3 ratio), which is within the range of 500 - 900 kg/m³ specified in the EN 323 standard. - **Mechanical properties**: - The bending strength (MOR) and elastic modulus (MOE) are significantly improved. Especially for the 1:3 ratio formula, MOR reaches 31 MPa and MOE reaches 2392 MPa, far exceeding the requirements of EN 310 and EN 316 standards. - **Dimensional stability**: - The thickness swelling rate (TS) reaches 5% after 24 - hour immersion in water, meeting the requirement of <25% in the EN 316 standard. - **Internal bond strength**: - The internal bond strength (IBS) reaches a maximum value of 0.98 MPa at the 3:1 ratio, meeting the minimum requirement of 0.40 MPa in the EN 319 standard. ### Statistical Analysis - Through one - way analysis of variance (ANOVA) and Duncan's multiple - range test (DMRT), the results show that different ratios of adhesives have a significant impact on the mechanical properties and dimensional stability of MDF, especially at the 95% - 99% confidence level. In conclusion, through optimizing the ratio of chitosan to epoxy resin, this research has successfully developed a formaldehyde - free MDF plate with excellent physical and mechanical properties, providing a new solution for replacing traditional urea - formaldehyde resin.