Growth, investigation of calcium D-gluconate monohydrate-CDG crystals with shocked impact for electronic usage and the pure crystal for sensor application
SenthilKannan, K.
DOI: https://doi.org/10.1007/s10854-024-12579-4
2024-04-24
Journal of Materials Science Materials in Electronics
Abstract:The CDG – calcium D-Gluconate monohydrate is the orthorhombic type of crystalline specimen identified from single crystal XRD grown by slow evaporation methodology; the 2 MPa pressure with 2.2 Mach number of shock wave pulses with 864 K temperature of which three versatile categories of 50, 100, and 150 scalings are preceded with the CDG sample and are represented after applied shock wave pulses as CDG-50; CDG-100 and CDG-150. The single crystal XRD of pure CDG is 6.7123, 13.3648, and 19.5447 in Å for bond lengths and bond angles are 90° each with P2 1 2 1 2 1 space group; orthorhombic system for CDG-50, CDG-100, and CDG-150 is 6.7167, 13.3747, and 19.5886, 6.7201, 13.3808, and 19.5898, and 6.7278, 13.3888, and 19.5977, respectively, and angles are same as 90°; and lengths are in Å units. The transparent nature of the materials of the CDG-50 is of 218 nm, the CDG-100 is of 221 nm cut-off wavelength, and finally the CDG-150 is of 220 nm wavelength. The corresponding photonic case of utilization is identified as 5.62 eV, 5.64 eV, and 5.68 eV, respectively, for CDG-50, CDG-100, and CDG-150. The fluorescence analysis of the all CDG shock pulsed samples having bandgap values pertaining to all CDG samples as 2.6956 eV, 2.8440 eV and 2.7312 eV, respectively, for bluish emission for all. The SEM of all samples is free from flaws and rod / bar-like pattern and thorny bar-like structures are observed. The CDG-50, CDG-100, and CDG-150 specimens are of negative photoconductivity type of classification. Dielectric characteristics are measured, and variations may be due to increased defects because of the high applied pressure by shock waves. The red LED with photodetector source for macro-scaled CDG's sensor analysis is studied and reported.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied