Thermal recovery of colour centres induced in cubic yttria-stabilized zirconia by charged particle irradiations

Francois Beuneu,Jean-Marc Costantini

DOI: https://doi.org/10.1088/0953-8984/18/15/013

2006-03-31

Abstract:We have used electron paramagnetic resonance to study the thermal annealing of colour centres induced in cubic yttria-stabilized zirconia by swift electron and heavy ion-irradiations. Single crystals were irradiated with 1 or 2-MeV electrons, and 200-MeV 127I, or 200-MeV 197Au ions. Electron and ion beams produce the same colour centres: namely i) an F+-like centre, ii) the so-called T-centre (Zr3+ in a trigonal oxygen local environment), and iii) a hole center. Isochronal annealing was performed up to 973 K. Isothermal annealing was performed at various temperatures on samples irradiated with 2-MeV electrons. The stability of paramagnetic centres increases with fluence and with a TCR treatment at 1373 K under vacuum prior to the irradiations. Two distinct recovery processes are observed depending on fluence and/or thermal treatment. The single-stage type I process occurs for F+-like centres at low fluences in as-received samples, and is probably linked to electron-hole recombination. T-centres are also annealed according to a single-stage process regardless of fluence. The annealing curves allow one to obtain activation energies for recovery. The two-stage type II process is observed only for the F+-like centres in as-received samples, at higher fluences, or in reduced samples. These centres are first annealed in a first stage below 550 K, like in type I, then transform into new paramagnetic centres in a second stage above 550 K. A simple kinetics model is proposed for this process. Complete colour centre bleaching is achieved at about 1000 K.

Materials Science

What problem does this paper attempt to address?

### What problems does this paper attempt to solve?

This paper mainly studied the thermal recovery process of colour centres induced by fast electrons and heavy - ion irradiation in yttria - stabilized zirconia (YSZ) single crystals. Specifically, the authors studied the annealing behavior of these colour centres at different temperatures through electron paramagnetic resonance (EPR) technology and attempted to answer the following key questions:

1. **Stability of colour centres**:
- How stable are different types of colour centres (such as F + - like centres, T - centres and hole centres) under different irradiation conditions (energy, dose)?
- Is the stability of these colour centres affected by the pre - performed high - temperature vacuum treatment (TCR treatment)?

2. **Mechanism of the annealing process**:
- What is the annealing process of colour centres at different temperatures? Are there different annealing stages?
- What are the kinetic models of these annealing processes? Can they be described by simple reaction kinetic equations?

3. **Interaction between colour centres**:
- Is there an interaction between F + - like centres and T - centres? How does this interaction affect their annealing behavior?
- In samples with high - dose irradiation or after TCR treatment, will F + - like centres be transformed into new defect centres?

4. **Determination of activation energy**:
- Can the activation energy of different colour centres be obtained from the annealing curves? Are these activation energies consistent with the known oxygen vacancy migration energy?

### Main findings

The main findings of the paper include:

- **Two annealing processes**:
- **Type I process**: This is a single - stage annealing process, applicable to F + - like centres in low - dose irradiated samples and T - centres at all doses. This process can be well described by a first - order reaction kinetic model.
- **Type II process**: This is a two - stage complex annealing process, only observed in samples with high - dose irradiation or after TCR treatment. The first stage is similar to Type I, and the second stage is accompanied by the transformation of F + - like centres into new defect centres.

- **Stability of colour centres**:
- As the irradiation dose increases, the stability of colour centres increases. In particular, the colour centres in samples after TCR treatment are more stable.

- **Activation energy**:
- By fitting the annealing curves, the activation energies of different colour centres were obtained. For example, the activation energy of F + - like centres is between 0.27 eV and 0.59 eV, and the activation energy of T - centres is approximately 0.57 eV.

### Conclusion

Through detailed experimental and theoretical analysis, the authors revealed the thermal recovery mechanism of colour centres in YSZ single crystals and proposed the corresponding kinetic models. These results are helpful for understanding the formation and evolution of defects in materials under irradiation conditions and are of great significance for the development of radiation - resistant materials.