Exploring metastable phase formation: swift heavy ion effects on partially stabilized zirconia

N.S. Kirilkin,T.N. Vershinina,J.H. O'Connell,R.A. Rymzhanov,V.A. Skuratov,V.А. Boltueva,S.А. Ghyngazov
DOI: https://doi.org/10.1016/j.jnucmat.2024.155369
IF: 3.555
2024-08-28
Journal of Nuclear Materials
Abstract:Zirconium dioxide shows great potential for use in the nuclear power industry. It exhibits high radiation stability (neutron and heavy ions) and can withstand harsh environments. The paper presents a study on the effects of 710 MeV Bi ion irradiation on polycrystalline partially yttria-stabilized zirconia using the combination of experimental techniques - X-ray diffraction, transmission electron microscopy and Raman spectroscopy. It was revealed that bismuth ion induced tracks retain their crystalline structure and their density tends to saturate at ∼1×10 12 cm −2 . As a result of dense ionization stimulated structural modification a t → t'' phase transformation was observed. The radiation stability of t'' phase against swift heavy ion impact was found to be higher compared to the t phase. No amorphization was detected up to Bi ion fluence of 2×10 13 cm −2 .
materials science, multidisciplinary,nuclear science & technology
What problem does this paper attempt to address?