Coupling losses and transverse resistivity of multifilament YBCO coated superconductors

M. Polak,L. Krempasky,E. Usak,L. Jansak,E. Demencik,G. A. Levin,P. N. Barnes,D. Wehler,B. Moenter

DOI: https://doi.org/10.1088/1742-6596/43/1/145

2006-02-18

Abstract:We studied the magnetization losses of four different types of filamentary YBCO coated conductors. A 10 mm wide YBCO coated conductor was subdivided into 20 filaments by laser cutting. The separation of coupling loss from the total is possible because the energy loss per cycle in samples with electrically insulated filaments has a very small frequency dependence. We measured the frequency dependence of the total losses in the frequency range between 0.1 Hz and 500 Hz. The coupling loss was obtained from the total by subtracting the hysteresis loss. The latter was measured at low frequencies since only hysteresis loss is non-negligible at frequencies below 1 Hz. The transverse resistivity was determined from the coupling losses; it was assumed that the sample length is equal to half of the twist pitch. The values of transverse resistivity deduced from the loss data were compared with those obtained by the four-point measurements with current flowing perpendicular to the filaments. Preliminary results indicate that the current method of laser ablation creates electrical contacts between the superconducting filaments and the substrate. This was also confirmed by the Hall probe mapping of the magnetic field in the vicinity of the tape. The measured transverse resistivity was close to the resistivity of the substrate (Hastelloy).

Superconductivity,Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the frequency - dependence of coupling loss and transverse resistivity in multi - filament YBCO - coated superconductors. Specifically, the researchers experimentally measured the total losses of four different types of multi - filament YBCO - coated conductors in the frequency range from 0.1 Hz to 608 Hz, and paid special attention to the characteristics of the coupling loss. The coupling loss was obtained by subtracting the hysteresis loss at low frequencies from the total loss, because the hysteresis loss is significant only when the frequency is lower than 1 Hz. In addition, the study also verified these results by comparing the transverse resistivity (\(\rho_{tr}\)) derived from the loss data with the values obtained by the four - point measurement method, which was carried out when the current flowed perpendicular to the filaments. Preliminary results show that there is electrical contact between the superconducting filaments and the substrate in some sample areas, which was also confirmed in the magnetic field mapping near the strip. Through these studies, the authors hope to better understand the loss mechanisms in multi - filament YBCO - coated conductors, especially the influence of coupling loss and their impact on material properties.