Abstract:Four different thin film nanocomposite (TFN) membranes were prepared by adding different concentrations of porous Zr-MOFs (UiO-66 and UiO-66-NH2) to piperazine (PIP) aqueous solution (aqueous phase) or 1,3,5-Benzenetricarbonyl trichloride (TMC)-n-hexane solution (organic phase) by interfacial polymerization. The main purpose is to study the specific effects of different addition methods and addition amounts of nanoparticles on the structure and performance of the TFN membranes by interfacial polymerization. All four TFN membranes exhibited higher water permeability while maintaining high salt rejection compared to thin film composite (TFC) membrane. On the one hand, the TFN membranes behaves differently which are prepared by adding the same kind of nanoparticles to the aqueous phase or organic phase, respectively. The TFN membrane prepared by adding 0.2 w/v% UiO-66 to the organic phase had high water flux of 87.86 L·m-2·h-1, comparing 46.31 L·m-2·h-1 of membrane prepared by adding 0.3 w/v% UiO-66 in the aqueous phase. This is due to the fact that UiO-66 greatly slows the interfacial polymerization rate when UiO-66 is added to the organic phase, resulting in a thinner and more aperture polyamide thin film layer, reducing the water transmission resistance during filtration. Therefore, it is more economical by adding nanoparticles to organic phase than aqueous phase under the same filtering effect. On the other hand, different nanoparticles can also cause differences in performance and structure of the TFN membranes even in the same preparation manner. TFN membrane with UiO-66-NH2 in the aqueous phase has higher water permeance than the one with UiO-66 in the aqueous phase, owning to good hydrophilicity of amino group, which improves the water dispersibility of UiO-66-NH2, so that the TFN membrane is more uniform. In addition, UiO-66-NH2 slows down the process of interface polymerization, making the membrane more porous. The monomers in aqueous phase and the organic phase can be adsorbed in the pores of Zr-MOFs, which makes the interfacial polymerization occur both in the pores and on the surface of the pores. Thus, the compatibility between the polyamide and MOFs was enhanced and less defects was formed in the thin film layer, resulting in high salt rejection even the concentration of Zr-MOFs increased. This is the first time to explain that polyamide membrane has not obvious salt rejection attenuation with increasing porous material content using pore adsorption reaction monomer principle. Also, the Zr-MOFs based TFN membrane exhibited good heat resistance and anti-fouling property. This work shows that porous Zr-MOFs nanomaterials have significant advantages in the development of nanofiltration membranes with high water flux and rejection.

Fabrication of water-stable MOF-808 membrane for efficient salt/dye separation

A backbone support structure and capillary effect-induced high-flux MOF-based mixed-matrix membrane for selective dye/salt separation

Designing heterogeneous MOF-on-MOF membrane with hierarchical pores for effective water treatment

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Stable Zr-Based Metal–Organic Framework Nanoporous Membrane for Efficient Desalination of Hypersaline Water

Highly Water-Permeable Metal–Organic Framework MOF-303 Membranes for Desalination

Preparation of Metal–Organic Framework/Polyvinylidene Fluoride Mixed Matrix Membranes for Water Treatment

Zeolite Imidazolate Frameworks-8@SiO2-ZrO2 Crystal-Amorphous Hybrid Core-Shell Structure as a Building Block for Water Purification Membranes

Fabrication of PVDF@MOF-303 membrane with Mortise-Tenon structure by the polyphenol analogue-assisted growth strategy for oil-water separation and heavy metal adsorption

Protein–polyphenol nanoassemblies modulated construction of zeolitic imidazole framework-67 based nanofiltration membrane for effective separation of dye/salt mixtures

Study on the properties of a nanofiltration membrane with O-MoS2 nanocomposite substrate and the applications in dye wastewater treatment

Construction of highly water-stable metal-organic framework UiO-66 thin-film composite membrane for dyes and antibiotics separation

Forward osmosis membrane doped with water-based zirconium fumarate MOFs to enhance dye pollutant removal and membrane antifouling performance

Enhancing contaminant rejection efficiency with ZIF-8 molecular sieving in sustainable mixed matrix membranes

Confined‐Coordination Induced Intergrowth of Metal‐Organic Framework into Precise Molecular Sieving Membranes

Cationic covalent organic framework membranes for efficient dye/salt separation

Crystal seeds induced interfacial growth of zirconium Metal–Organic framework membranes towards efficient hydrogen purification

Ultrathin water-stable metal-organic framework membranes for ion separation.

Membrane adsorbers with ultrahigh metal-organic framework loading for high flux separations

Porous Zr-based metal organic frameworks (Zr-MOFs) incorporated thin film nanocomposite membrane toward enhanced desalination performance.

MOF-808/Polyamide Thin-Film Nanocomposite Membranes for Efficient Nanofiltration