Abstract:Czochralski (CZ) silicon is a base material for manufacturing integrated circuits (ICs). The mechanical strength of CZ silicon determines the processing limitations and often dominates the issues related to packaging and failure of ICs. With the ever-smaller feature size of ICs, the scaling of device dimensions may indirectly lead to increase the stress in silicon substrate, thus increasing the probability of generating dislocations. Consequently, improving the mechanical strength of CZ silicon is of significance for increasing the manufacturing yield of ICs. In this work, we propose a strategy of co-doping germanium (Ge) impurity and nitrogen (N) impurity into CZ silicon to achieve better mechanical strength. In order to explore the feasibility of such a strategy, we comparatively investigate the room-temperature hardness and dislocation gliding behaviors in the temperature range of 600–1200 ℃ in the conventional CZ silicon, Ge-doped CZ silicon, N-doped CZ silicon, as well as N and Ge co-doped CZ silicon. The significant experimental results are described as follows. 1) Ge-doping, N-doping or co-doping of Ge and N hardly influences the hardness and therefore the dislocation gliding behavior at room temperature. 2) The suppressing effect of N-doping on the dislocation gliding is remarkable at 600–1000 ℃ and becomes weakened at the temperatures higher than 1100 ℃, while Ge-doping hardly affects the dislocation gliding at 600–900 ℃ but exhibits a strong suppressing effect on the dislocation gliding at 1000–1200 ℃. 3) Co-doping Ge and N impurities into CZ silicon can take the complementary advantages of both Ge- and N-doping to suppress the dislocation gliding at 600–1200 ℃. It is believed that N-doping can result in the formation of N-O complex-related pinning agents within the dislocation cores to suppress the dislocation gliding at 600–1000 ℃. For Ge-doping, it is supposed that Ge-O complexes acting as the pinning agents can form near the front of a single dislocation when the temperature is as high as 1000 ℃ and above. In a word, it is verified in this work that co-doping Ge and N into CZ silicon can further improve the mechanical strength at the processing temperatures of ICs fabrication.

Effects of Nitrogen Doping on Pulling Rate Range of Defect-Free Crystal in CZ Silicon

Extended Defects in Nitrogen-Doped Czochralski Silicon During Diode Process

Oxygen Precipitation in Nitrogen Doped Czochralski Silicon Wafers. I. Formation Mechanisms of Near-Surface and Bulk Defects

Mechanical Strength of Czochralski Silicon Crystal: Effects of Co-Doping Germanium and Nitrogen

Effects of Co-Doping Nitrogen and Germanium on Dislocation Gliding in Czochralski Silicon: Implication for Improving Mechanical Strength

Mechanical strength of nitrogen-doped silicon single crystal investigated by three-point bending method

Defect structure of nitrogen doped czochralski silicon annealed under enhanced pressure

Process-induced defects in nitrogen doped Czochralski silicon in diode processes

Nitrogen Effect on Self-Interstitial Generation in Czochralski Silicon Revealed by Gold Diffusion Experiments

Effect of Nitrogen Doping on Denuded Zone Formed by Rapid Thermal Process in Czochralski Silicon Wafer

Nitrogen in Czochralski Silicon

Role of Nitrogen Related Complexes in the Formation of Defects in Silicon

Grown-In Defects in Nitrogen-Doped Czochralski Silicon

Effects of Nitrogen on Grown-in Oxygen Precipitates in Large Diameter Czochralski Silicon

Effect of Germanium Codoping on the Grown‐In Oxide Precipitates in Nitrogen‐Doped Czochralski Silicon

Effect Of Nitrogen Doping On The Dissolution Of Oxygen Precipitates In Czochralski Silicon During Rapid Thermal Annealing

Effects of Nitrogen Doping on Vacancy-Oxygen Complexes in Neutron Irradiated Czochralski Silicon

Effect of Nitrogen on Denuded Zone in Czochralski Silicon Wafer

Effect of Nitrogen Doping on Oxygen Precipitate Profiles in Czochralski Silicon Wafer

On the Assumed Impact of Germanium Doping on Void Formation in Czochralski-Grown Silicon

Rapid-Thermal-Processing-Based Intrinsic Gettering For Nitrogen-Doped Czochralski Silicon