Graphitic Carbon-Doped Mesoporous Fe 2 O 3 Nanoparticles for Long-Life Li-Ion Anodes
Gang Xu,Jia-Bin Sun,Guo-Yan Wang,Xian-Fa Zhang,Zhao-Peng Deng,Li-Hua Huo,Shan Gao
DOI: https://doi.org/10.1021/acsanm.1c00649
IF: 6.14
2021-06-28
ACS Applied Nano Materials
Abstract:Biomass carbon-coated and pseudocapacitance-assisted α-Fe<sub>2</sub>O<sub>3</sub> has recently gained more attention for enhanced lithium storage performance. Herein, we used a waste poplar branch as a biotemplate and a carbon source to prepare graphitic-C-doped mesoporous α-Fe<sub>2</sub>O<sub>3</sub> (α-Fe<sub>2</sub>O<sub>3</sub>/C) through a simple immersion–carbonization–calcination method. The influence of carbon content on both the microstructures and electrochemical properties was also studied. The product calcined in air at 400 °C (Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub>) presents a hierarchically tubular structure with cross-linkage of 18% graphitic-C and α-Fe<sub>2</sub>O<sub>3</sub> nanoparticles with an average size of ∼28 nm. Meanwhile, the Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub> nanomaterial exhibits a large surface area of 114 m<sup>2</sup> g<sup>–1</sup> and mesopore size distribution centered at 2 nm. As lithium-ion battery anode material, such a unique hierarchical structure presents a certain pseudocapacitance behavior, thus improving its lithium storage performance. Electrochemical measurements show that the Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub> nanomaterial exhibits higher specific capacity and better rate performance. Especially, it can retain a capacity of 885 mA h g<sup>–1</sup> at 1 A g<sup>–1</sup> after cycling 1400 times, indicating good capacity retention and long-cycling stability. The good electrochemical performance mainly originates from the synergism of the unique microstructure of the Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub> nanomaterial, suitable doping of graphitic-C, and certain pseudocapacitance behavior. Thus, the low-cost bifunctional biotemplate strategy can provide a useful experience for the massive synthesis of pseudocapacitance-assisted high-performance anodes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.1c00649?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.1c00649</a>.Material characterization, assembly and electrochemical test of half-cells; XPS spectra of Fe<sub>2</sub>O<sub>3</sub>/C<sub>450</sub> (Figure S1); N<sub>2</sub> adsorption–desorption isotherm and pore size distribution of Fe<sub>2</sub>O<sub>3</sub>/C<sub>450</sub> (Figure S2); long-cycling discharge performance of the Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub> electrode at 3.0 A g<sup>–1</sup> (Figure S3); TG curve in air, XRD pattern, and cyclic performance of Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub>-1 h electrode at 1.0 A g<sup>–1</sup> (Figure S4); Li<sup>+</sup>-ion diffusion coefficient (Figure S5); TEM images of Fe<sub>2</sub>O<sub>3</sub>/C<sub>400</sub> and Fe<sub>2</sub>O<sub>3</sub>/C<sub>450</sub> electrodes before and after cycling 1000 times (Figure S6); and comparison of long cycle performance of carbon-doped Fe<sub>2</sub>O<sub>3</sub> composites (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.1c00649/suppl_file/an1c00649_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology