Abstract:Hard carbon (HC) stands out as the preeminent anode material for sodium-ion batteries (SIBs) which are deployed in expansive energy storage infrastructures. Herein, the large enough graphene nanosheets interlayer and abundant nanopores with a diameter of ∼2.1 nm induced by adjusting the pyrolysis temperature in the thermosetting phenolic resin-derived hard carbon matrix to augment the performance of the sodium ion storage. The presence of sufficiently large carbon interlayers has been proven to provide active sites for reversible adsorption, enabling effective storage of sodium ions in the high-voltage slope region, while also promoting rapid Na + transport. Meanwhile, forming abundant closed nanopores with larger sizes helps sodium ion storage in the low-voltage plateau region. In the optimized samples, the formation of sufficient long graphene nanosheets with a perfect crystal lattice, which further shrinks to form enclosed nanopores, effectively reduces defective sites and specific surface area. Additionally, the appropriate content of C-O and C=O functional groups contributes to an exceptional initial Coulombic efficiency (ICE) of up to 93%. Simultaneously, the optimized sample HC-1500 contributes to a remarkable plateau capacity of 294 mAh g - 1 during the charging process (high reversible capacity of 403 mAh g - 1 at 0.1 C). Moreover, based on the microstructure evolution and Na storage behavior of hard carbon, an "adsorption (27%) – filling (73%)" sodium storage mechanism that the sodium storage as a quasi-metallic sodium state is demonstrated. Consequently, this study will offer valuable insights for the development of hard carbon anodes tailored for high-energy practical SIBs, while also advancing the understanding of sodium storage mechanisms.

Hierarchical Porous Carbon Anode Materials Derived from Rice Husks with High Capacity and Long Cycling Stability for Sodium‐Ion Batteries

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

Hierarchical porous hard carbon derived from rice husks for high-performance sodium ion storage

A Hierarchical N/S‐Codoped Carbon Anode Fabricated Facilely from Cellulose/Polyaniline Microspheres for High‐Performance Sodium‐Ion Batteries

Sodium‐Ion Batteries: Hard–Soft Carbon Composite Anodes with Synergistic Sodium Storage Performance (adv. Funct. Mater. 24/2019)

Ultrahigh Plateau‐Capacity Sodium Storage by Plugging Open Pores

Sustainable Fabrication of a Practical Hard Carbon Anode for a Sodium-Ion Battery with Unprecedented Long Cycle Life

Hard Carbon/graphene Microfibers As a Superior Anode Material for Sodium-Ion Batteries

Biomass derived hard carbon used as a high performance anode material for sodium ion batteries

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

Understanding the Sodium Storage Behavior of Closed Pores/Carbonyl Groups in Hard Carbon

Scalable synthesis of N/S co-doped hard carbon microspheres as a high-performance anode material for sodium-ion batteries

Nitrogen/Phosphorus Dual‐Doped Hard Carbon Anode with High Initial Coulombic Efficiency for Superior Sodium Storage

Hierarchical porous hard carbon enables integral solid electrolyte interphase as robust anode for sodium-ion batteries

A Stable Biomass‐Derived Hard Carbon Anode for High‐Performance Sodium‐Ion Full Battery

Hard Carbon Reprising Porous Morphology Derived from Coconut Sheath for Sodium-Ion Battery

Hard carbon derived from waste tea biomass as high-performance anode material for sodium-ion batteries

Lotus Seedpod-Derived Hard Carbon with Hierarchical Porous Structure as Stable Anode for Sodium-Ion Batteries

3D connected porous structure hard carbon derived from paulownia xylem for high rate performance sodium ion battery anode

From Natural Fibers to High-Performance Anodes: Sisal Hemp Derived Hard Carbon for Na-/K-Ion Batteries and Mechanism Exploration

Extended low-voltage plateau capacity of hard carbon spheres anode for sodium ion batteries