Solvent-Resistant Lignin-Epoxy Hybrid Nanoparticles for Covalent Surface Modification and High-Strength Particulate Adhesives

Tao Zou,Mika Henrikki Sipponen,Alexander Henn,Monika Österberg,Monika Österberg

DOI: https://doi.org/10.1021/acsnano.0c09500

IF: 17.1

2021-02-17

ACS Nano

Abstract:Fabrication of spherical lignin nanoparticles (LNPs) is opening more application opportunities for lignin. However, dissolution of LNPs at a strongly alkaline pH or in common organic solvent systems has prevented their surface functionalization in a dispersion state as well as processing and applications that require maintaining the particle morphology under harsh conditions. Here, we report a simple method to stabilize LNPs through intraparticle cross-linking. Bisphenol A diglycidyl ether (BADGE), a cross-linker that, like lignin, contains substituted benzene rings, is coprecipitated with softwood Kraft lignin to form hybrid LNPs (hy-LNPs). The hy-LNPs with a BADGE content ≤20 wt % could be intraparticle cross-linked in the dispersion state without altering their colloidal stability. Atomic force microscopy and quartz crystal microbalance with dissipation monitoring were used to show that the internally cross-linked particles were resistant to dissolution under strongly alkaline conditions and in acetone-water binary solvent that dissolved unmodified LNPs entirely. We further demonstrated covalent surface functionalization of the internally cross-linked particles at pH 12 through an epoxy ring-opening reaction to obtain particles with pH-switchable surface charge. Moreover, the hy-LNPs with BADGE content ≥30% allowed both inter- and intraparticle cross-linking at &gt;150 °C, which enabled their application as waterborne wood adhesives with competitive dry/wet adhesive strength (5.4/3.5 MPa).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c09500?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c09500</a>.Table showing the preparation parameters, final obtained concentrations, and yields of the hy-LNPs and LNPs; volume-based hydrodynamic diameter distributions and ζ potential distributions of the hy-LNPs and LNPs; colloidal stability of the hy-LNPs in aqueous media at various temperatures; vuring of hy-LNPs10 in dispersion state and their resistance to acetone-water (3:1, w/w) after curing; table showing the average particle heights of 0.5–8 h cured hy-LNPs20, before and after rinsing with acetone-water (3:1, w/w); IR absorption of 0 to 8 h cured hy-LNPs20; <i>D</i>_h and ζ potential of the uncured and 4 h cured hy-LNPs20; DLS results of the uncured hy-LNPs20 at pH 12.9; scanning electron microscopic images of the veneer surfaces with and without cured hy-LNPs30; photo showing the wood failure occurring to the 0.8 mm-thick veneers during adhesive strength test; DSC results of the hy-LNPs, mechanically blended SKL and BADGE mixture, BADGE (in solid form) and SKL; AFM and ATR-FTIR results of the hy-LNPs and LNPs after various heat-treatments; ³¹P NMR and XPS results of the untreated and heat-treated LNPs; SKL molar mass distribution determined with GPC (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c09500/suppl_file/nn0c09500_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology