Enhancing polymeric bone scaffolds mechanical characteristics using supercritical CO 2 foaming and reinforcing agents
F. Carrascosa,M.T. García,M.J. Ramos,J.M. García-Vargas,J.F. Rodríguez,I. Gracia
DOI: https://doi.org/10.1016/j.jtice.2024.105619
IF: 5.477
2024-06-21
Journal of the Taiwan Institute of Chemical Engineers
Abstract:Highlights • scCO 2 foaming and melt-extrusion were used to produce reinforced scaffolds. • Creation of foams with high-porosity, homogeneity and reinforcement. • Pressure had a significant influence on pore size and compressive strength. • Stresses similar to trabecular bone were obtained for Mg(OH) 2 and HAp foams. Background As an alternative to conventional medicine, scaffolds have emerged to mimic and/or replace damaged tissue. 3D porous matrix scaffolds made of biodegradable and biocompatible polymers, including PLGA, have proven to be of particular interest for use as bone substitutes in Tissue Engineering. Methods The study used high-pressure CO 2 foaming to produce PLGA-based foams. Previously, melt-extrusion was used to introduce reinforcement agents, Mg(OH) 2 , Hydroxyapatite (HAp) and Mg, to achieve foams with improved properties. Foam morphology was analysed using SEM, EDS, and 3D scanner techniques, and foam strength was measured using compression tests. A statistical analysis was carried out to study the effect of pressure and temperature on foams pore size and hardness. Significant findings The foams produced were rigid, non-sticky and time-stable, and showed high porosity. The pressure was found to be the only significant variable to tune both porosity and cell densities of scaffolds. Setting a pore size at 500 μm, compressive stresses of 1.85 MPa, 3.81 MPa were achieved for Mg(OH) 2 and HAp, respectively. Those results were comparable to literature ́s trabecular bovine bone compression resistance of 4.2 MPa. This finding indicated the possibility of getting, at the same time, convenient results for porosity and mechanical resistance for their use as bone replacement agents. Finally, a 20 % w/w ratio of reinforcing agent was found to produce the best pore size-stress ratio. Graphical abstract Download : Download high-res image (182KB) Download : Download full-size image
engineering, chemical