Abstract:Atomic and electronic structures of a polar surface of MgO formed on Ag(111) was investigated by using reflection high energy electron diffraction (RHEED), Auger electron spectroscopy, electron energy loss spectroscopy (EELS), and ultraviolet photoemission spectroscopy (UPS). A rather flat unreconstructed polar MgO(111) 1$\times$1 surface could be grown by alternate adsorption of Mg and O$_{2}$ on Ag(111). The stability of the MgO(111) surface was discussed in terms of interaction between Ag and Mg atoms at the interface, and charge state of the surface atoms. EELS of this surface did not show a band gap region, and finite density of states appeared at the Fermi level in UPS. These results suggest that a polar MgO(111) surface was not an insulating surface but a semiconducting or metallic surface.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: how to grow an unreconstructed polar MgO(111) thin film on an Ag(111) substrate and study its atomic and electronic structures. Specifically, the researchers focus on the following points:
1. **Growth method**: Prepare the MgO(111) thin film by alternately adsorbing magnesium (Mg) and oxygen (O₂) on the Ag(111) substrate.
2. **Stability mechanism**: Explore the stability of this polar surface, especially when polar surfaces are theoretically considered to be unstable.
3. **Electronic structure**: Study the electronic structure of the MgO(111) surface, especially how it differs from that of the non - polar MgO(100) surface.
### Detailed Explanation
#### 1. Growth method
The researchers adopted an alternate deposition method to deposit magnesium and oxygen successively on the Ag(111) substrate. This method enables the MgO(111) thin film to grow at a relatively low temperature (300 K) and form an unreconstructed, flat (111) surface. The grown thin film was characterized by techniques such as reflection high - energy electron diffraction (RHEED), Auger electron spectroscopy (AES), electron energy - loss spectroscopy (EELS) and ultraviolet photoelectron spectroscopy (UPS).
#### 2. Stability mechanism
Normally, polar surfaces are unstable due to the existence of macroscopic electric fields. However, the study found that the MgO(111) thin film can remain stable on the Ag(111) substrate. This is mainly attributed to the following factors:
- **Interface interaction**: The strong interaction between Mg and Ag atoms reduces the interface free energy, thus helping to stabilize the thin film.
- **Surface atomic charge state**: The charges of surface oxygen ions (O²⁻) and magnesium ions (Mg²⁺) are reduced, reducing the influence of the macroscopic electric field.
- **Image - charge effect**: The image charges on the metal substrate also help to stabilize the thin film, especially when the thickness is an odd number of layers.
#### 3. Electronic structure
Through EELS and UPS measurements, the researchers found that there are significant differences in the electronic structures between the MgO(111) surface and the MgO(100) surface:
- **Band - gap characteristics**: The MgO(111) surface has no obvious band - gap region, and a finite density of states appears near the Fermi level.
- **Conductive properties**: These results indicate that the MgO(111) surface is not an insulator, but more like a semiconductor or a metal surface. This phenomenon may be related to the change in the Madelung potential, which leads to a reduction in the band - gap and thus makes the surface conductive.
In conclusion, through experimental and theoretical analysis, this paper reveals the possibility of growing an unreconstructed polar MgO(111) thin film on an Ag(111) substrate and its unique electronic structure characteristics.