Abstract:The long-term periodicity and uncontrollable interface properties during the preparation process for silicon carbide fiber reinforced silicon carbide-based composites (SiCf/SiC CMC) make it difficult to thoroughly investigate their mechanical damage behavior under complex loading conditions. To delve deeper into the influence of the interface strength and toughness on the mechanical response of microscopic representative volume element (RVE) models under complex loading conditions, in this work, based on numerical simulation methods, a microscale representative volume element (RVE) with periodic symmetric boundary conditions for the material is constructed. The phase-field fracture theory and cohesive zone model are coupled to capture the brittle cracking of the matrix and the debonding behavior at the fiber/matrix interface. Simulation analysis is conducted for tensile, compressive, and shear loading as well as combined loading, and the validity of the model is verified based on the Chamis theory. Further investigation is conducted into the mechanical response behavior of the microscale RVE model under complex loading conditions in relation to the interface strength and interface toughness. The results indicate that under uniaxial loading, increasing the interface strength leads to a tighter bond between the fiber and matrix, suppressing crack initiation and propagation, and significantly increasing the material's fracture strength. However, compared to the transverse compressive strength, increasing the interface strength does not continuously enhance the strength under other loading conditions. Meanwhile, under the condition of strong interface strength of 400 MPa, an increase in the interface toughness significantly increases the transverse compressive strength of the material. When it increases from 2 J/m2 to 20 J/m2, the transverse compressive strength increases by 28.49%. Under biaxial combined loading, increasing the interface strength significantly widens the failure envelope space under σ2-τ23 combined loading; with the transition from transverse compressive stress to tensile stress, the transverse shear strength shows a trend of first increasing and then decreasing, and when the ratio of transverse shear displacement to transverse tensile/compressive displacement is −1, it reaches the maximum. This study provides strong numerical support for the investigation of the interface properties and mechanical behavior of SiCf/SiC composites under complex loading conditions, offering important references for engineering design and material performance optimization.

Prediction of effective cohesive parameters for mode I failure behavior of LPBF Ti-6Al-4 V/CFRTP interface using meso -scale modelling

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

PHASE FIELD BASED COHESIVE ZONE FRACTURE APPROACH TO MODEL ANISOTROPIC EFFECT AND INTERFACE FRACTURE IN FIBER REINFORCED POLYMER COMPOSITES

Computational Micromechanics-Based Prediction of the Failure of Unidirectional Composite Lamina Subjected to Transverse and In-Plane Shear Stress States

Fatigue life prediction for LPBF-fabricated Ti-6Al-4V up to very-high-cycle regime based on continuum damage mechanics incorporating effect of defects

Evaluation of the critical SERR in the presence of heterogeneous interfaces in bonded joints: application to parallel defects in DCB titanium alloy laser-treated specimens

A micromechanics-based interface mesomodel for virtual testing of laminated composites

Effect of interfacial nanostructure on mode mixity in directly bonded carbon fiber reinforced thermoplastic laminates and aluminum alloy considering thermal residual stress

Mixed-mode failure of interfaces studied by the 2D linear elastic–brittle interface model: Macro- and micro-mechanical finite-element applications in composites

The Influence of the Interface on the Micromechanical Behavior of Unidirectional Fiber-Reinforced Ceramic Matrix Composites: An Analysis Based on the Periodic Symmetric Boundary Conditions

Cohesive Zone Model Prediction of Debonding Failure in CFRP-to-steel Bonded Interface with a Ductile Adhesive

Micromechanics-Based Modeling of Interfacial Debonding in Multilayer Structures

Cohesive Zone Modeling of the Interface Fracture in Full-Thermoplastic Hybrid Composites for Lightweight Application

Experimental and theoretical study on residual ultimate strength after impact of CF/PEEK-titanium hybrid laminates with nano-interfacial enhancement

Influence of Failure-Load Prediction in Composite Single-Lap Joints with Brittle and Ductile Adhesives Using Different Progressive-Damage Techniques

Multi-scale analysis of the adhesive bonding behavior of laser surface-treated carbon fiber reinforced polymer composite structures

Fracture Toughness of a Corrugate Interface Between Two Dissimilar Materials

Experimental and numerical study on the tensile failure behavior of toughened-interlayer composite laminates with automated fiber placement (AFP) induced gap and overlap defects

Interfacial debonding in a thin plate bonded to a rigid substrate with a circular hole

Porosity estimation of a micro-cracked adhesive interface by μCT scanning: Comparison between experimentally measured effective stiffnesses and those predicted by an imperfect interface model

Cohesive Fracture Simulation and Failure Modes of FRP–concrete Bonded Interfaces