Abstract:We report on the synthesis of high quality La$_{1/3}$Sr$_{2/3}$FeO$_3$ (LSFO) thin films using the pulsed laser deposition technique on both SrTiO$_3$ (STO) and LaAlO$_3$ (LAO) substrates (100)-oriented. From X-Ray diffraction (XRD) studies, we find that the films have an out-of-plane lattice parameter around 0.3865nm, almost independent of the substrate (i.e. the nature of the strains). The transport properties reveal that, while LSFO films deposited on STO exhibit an anomaly in the resistivity vs temperature at 180K (corresponding to the charge-ordered transition and associated with a transition from a paramagnetic to an antiferromagnetic state), the films grown on LAO display a very small magnetoresistance behavior and present an hysteresis around 270K under the application of a 4T magnetic field. The changes in transport properties between both substrates are discussed and compared with the corresponding single crystals.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to grow high - quality La\(_{1/3}\)Sr\(_{2/3}\)FeO\(_3\) (LSFO) thin films on different substrates by pulsed - laser deposition (PLD) and study their structural and transport properties. Specifically, the authors focus on the following issues:
1. **Quality of thin - film growth**: How to grow high - quality LSFO thin films on different substrates such as SrTiO\(_3\) (STO) and LaAlO\(_3\) (LAO).
2. **Influence of lattice parameters**: Explore the influence of substrate - induced strain on the epitaxial growth of LSFO thin films and their lattice parameters. In particular, study whether different substrates (compressive or tensile strain) will affect the lattice constant of the thin films.
3. **Change in transport properties**: Analyze the relationship between the resistivity and temperature of LSFO thin films on different substrates, especially whether there is abnormal behavior at low temperatures, such as charge - ordered transition (CO) and magnetic transition.
4. **Magnetoresistance effect**: Study the magnetoresistance (MR) effect of LSFO thin films on different substrates and compare these effects with those of single - crystal materials.
5. **Stability of the charge - ordered state**: Evaluate the influence of different substrates on the charge - ordered state (CO state) in LSFO thin films, especially the change in the stability of this state under different strain conditions.
### Specific problem analysis
- **Substrate selection**: The authors selected two different substrates - SrTiO\(_3\) (STO) and LaAlO\(_3\) (LAO), applying compressive strain and tensile strain respectively, to study the influence of strain on the properties of LSFO thin films.
- **Structural characterization**: Through X - ray diffraction (XRD) measurement, the epitaxial growth quality and lattice parameters of the thin films were determined. The results show that although the substrates are different, the epitaxial growth quality of the thin films is high, and the lattice parameters in the epitaxial direction are hardly affected by the substrate type.
- **Transport properties**:
- The LSFO thin film grown on the STO substrate shows an abnormal resistivity at around 180 K, corresponding to the charge - ordered transition (CO transition), accompanied by a transition from the paramagnetic state to the antiferromagnetic state.
- The LSFO thin film grown on the LAO substrate shows a smaller magnetoresistance effect and exhibits a thermal hysteresis phenomenon at around 270 K, which may be due to the charge - ordered transition.
- **Charge - ordered state**: Research shows that for the LSFO thin film grown on the STO substrate, the charge - ordered transition temperature (TCO) is lower, while for the film grown on the LAO substrate, the TCO is higher, indicating that the charge - ordered state is more stable under compressive strain.
### Conclusion
This study reveals the important influence of substrate strain on the structure and transport properties of LSFO thin films. In particular, the charge - ordered state is more stable under compressive strain and becomes unstable under tensile strain. These results provide important clues for understanding the charge - ordered phenomenon in transition - metal - oxide thin films and a theoretical basis for further optimizing the performance of these materials.