Abstract:In this study, we develop a roasting method for removing arsenic from sulfide copper-arsenic-containing materials. The object of the study was fine dust from copper smelting production of the following composition (wt%): 34.89 – Zn; 20.02 – Cu; 17.74 – Pb; 17.07 – Fe; 7.12 – As; 0.92 – Sb; 0.69 – Sn; 0.63 – Ca; 0.42 – Mo; and 0.34 – K. The chemical composition of the materials was analyzed using an SHIMADZU EDX-7000 energy dispersive X-ray fluorescence spectrometer and a Bruker D8 Advance diffractometer. The roasting process was carried out in a laboratory tube furnace at a temperature of 550–800°C for 60–120 minutes with the addition of 25–50% of FeS 2 to the charge. Optimal conditions for reducing residual arsenic in the calcine to less than 0.3 wt% were identified: a temperature of 750–800°C, a duration of 1.5–2.0 h (in an inert atmosphere), and the use of 30 wt% of pyrite concentrate in the charge. Arsenic removal to the gas phase reached 91–96%. It is shown that in order to reduce the processing temperature to 600°C, it is necessary to add a reducing agent (coke fines) to the mixture of copper smelting dust with pyrite or increase the proportion of pyrite in the test charge to 50 wt% and hold the mixture for 1.5–2.0 h under inert atmosphere (argon and nitrogen) or low-oxygen blast. Arsenic removal to the gas phase reached 97%. X-ray spectral analysis of the residue deposited on the cooled ends of quartz tubes following the release of gases formed during roasting revealed that this material is predominantly (up to 93%) composed of arsenic. The resulting calcine contained 94 wt% of iron, zinc, copper and lead compounds. Therefore, the calcine obtained during the roasting of fine dust from copper smelting production is suitable for returning to the copper production process.

Behavior of As, Pb, Cu, and Zn under conditions of reduction roasting of fine dust generated by a copper smelter with natural gas

Extraction of arsenic from fine dust of copper smelters by reduction roasting with natural gas

Extraction of Pb, Cu, Zn and As from Fine Dust of Copper Smelting Industry via Leaching with Sulfuric Acid

Effect of roasting parameters on arsenic removal from copper smelting dust

Extraction of non-ferrous metals and arsenic from fine dusts of copper smelter production by combined technology

Pyrometallurgical Recovery of Valuable Metals from Flue Dusts of Copper Smelter Through Lead Alloy

Recovery of Copper, Lead, Zinc, and Arsenic from Copper Smelting Dust by Oxidative Alkaline Leaching and Sulfide Precipitation

Iron extraction from dust from scrap metal smelting in electric arc furnaces by magnetic separation

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Quantitative characterization of secondary copper flue dust and guidance for separating valuable and toxic elements via low-temperature roasting and selective leaching

Element Distribution in Oxygen-Enriched Bottom-Blown Smelting of High-Arsenic Copper Dross

Removal of arsenic from dusts produced during the pyrometallurgical refining of copper by vacuum carbothermal reduction

A Review of the Comprehensive Recovery of Valuable Elements from Copper Smelting Open-Circuit Dust and Arsenic Treatment

Leaching and removal of arsenic with waste acids from arsenic pre-removed dusts discharged from furnaces for pyrometallurgical refining of copper

Strategies for arsenic pollution control from copper pyrometallurgy based on the study of arsenic sources, emission pathways and speciation characterization in copper flash smelting systems

Recovery of Copper, Lead and Zinc from Copper Flash Converting Slag by the Sulfurization-Reduction Process

Development of a Method for Reprocessing Technogenic Lead Production Raw Materials to Extract Rhenium and Arsenic

Co-treatment of copper smelting flue dust and arsenic sulfide residue by a pyrometallurgical approach for simultaneous removal and recovery of arsenic

Ultrasound-Assisted Selective Leaching of Arsenic from Copper Smelting Flue Dust

Removal behavior of Zn and alkalis from blast furnace dust in pre-reduction sinter process

Behavior of copper and lead during mineralurgical and hydrometallurgical processing of flash smelting slag