Abstract:Stable and efficient syngas production via methane dry reforming is highly desirable as it utilizes two greenhouse gases simultaneously. In this work, active Ni–Cu nanoalloys stably anchored on periclase-phase MgAlOx nanosheets were successfully synthesized by a hydrothermal method. These highly dispersed small Ni–Cu alloys strongly interacted with the periclase-phase MgAlOx nanosheets, on which abundant base sites were accessible. On the optimal catalyst (6Ni6CuMgAl–S), methane and carbon dioxide conversion always reached 85 and 90% at 700 °C under a gas hour speed velocity of 40,000 mL/gcat h for more than 70 h. The hydrogen production rate was maintained at 1.8 mmol/min, and the ratio of H2/CO was kept at approximately 0.96 under a CH4 and CO2 flow rate of 25 mL/min. Coke deposition and Ni sintering were effectively suppressed by the formation of a Ni–Cu alloy, the laminar structure, and the periclase phase of the MgAlOx support. Moreover, the alloy nanoparticles were reconstructed into a segregated Ni–Cu alloy structure in response to the reaction environment, and this structure was more stable and still active. Density functional theory calculations showed that carbon adsorption was inhibited on the segregated Ni–Cu alloy. Furthermore, the experimental thermogravimetric and O2-TPO results confirmed the significant decrease in carbon deposition on the Ni–Cu alloy catalysts.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c14918.DFT theoretical calculation; additional characterizations of some catalysts, including XRD patterns, SEM images, N2 adsorption, desorption, and pore size distribution; H2-TPR profiles; H2-TPD profiles; HAADF image and element mapping; TEM images; XPS spectra; acid property; and additional reaction data (PDF)This article has not yet been cited by other publications.

Synthesis and regeneration of mesoporous Ni–Cu/Al2O4 catalyst in sub-kilogram-scale for methanol steam reforming reaction

Synthesis of Mesoporous Cu-Ni/Al2O4 Catalyst for Hydrogen Production via Hydrothermal Reconstruction Route

Ni-based catalysts supported on MgAl<sub>2</sub>O<sub>4</sub> with different properties for combined steam and CO<sub>2</sub> reforming of methane

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Highly dispersed Ni/Al2O3 catalysts for dry reforming of methane prepared by alkaline-induced adsorption process

Oxidative Steam Reforming of Methanol over Cu-Based Catalysts

A Plate-Type Anodic Alumina Supported Nickel Catalyst for Methane Steam Reforming

Sustainable cement and clay support in Ni–Cu/Al 2 O 3 catalysts for enhancing hydrogen production from methanol steam reforming

Methane Dry Reforming by Ni–Cu Nanoalloys Anchored on Periclase-Phase MgAlO x Nanosheets for Enhanced Syngas Production

CO2 Reforming of Methane over a Highly Dispersed Ni/Mg-Al-O Catalyst Prepared by a Facile and Green Method

Statistical optimization of hydrogen production from bio-methanol steam reforming over Ni-Cu/Al2O3 catalysts

Insights into the Mechanism of Methanol Steam Reforming for Hydrogen Production over Ni–Cu-Based Catalysts

Highly Dispersed Ni Nanoparticles Supported by Porous Al2O3 Rods for Catalytic Dry Reforming of Methane

CuO modified LaNi0.4Al0.6O3‐δ with improvement performance in MSR at Low Temperature

NiCu Alloy/Perovskite Nanoparticle Catalyst for Methanol Steam Reforming via Prereduction and In Situ Exsolution Technology

Methane Dry Reforming by Ni-Cu Nanoalloys Anchored on Periclase-Phase MgAlO<i><sub>x</sub></i> Nanosheets for Enhanced Syngas Production

CO2 Methanation: Nickel–Alumina Catalyst Prepared by Solid-State Combustion

The Cu-Al2O3 Interface: an Unignorable Active Site for Methanol Steam Reforming Hydrogen Production

Ni-based bimetallic catalysts for hydrogen production via (sorption-enhanced) steam methane reforming

Ordered Mesoporous Alumina Supported Nickel Based Catalysts for Carbon Dioxide Reforming of Methane

Carbon-coated mesoporous silica-supported Ni nanocomposite catalyst for efficient hydrogen production via steam reforming of toluene