Phase relationship of quaternary system FeO-Al2O3-SiO2-‘V2O3’ at 1873 K and its impact during melting of H-DRI for possible vanadium extraction

J. Martinsson,A. Vickerfält,J. Huss

DOI: https://doi.org/10.62053/gbqb1648

2024-06-19

Proceedings

Abstract:The European Union has listed vanadium (V) as one of the critical raw materials for the transition to a future green society, as stated in the Critical Raw Material Act, written by Grohol and Veeh. In the steelmaking industry based on V-containing iron ore, V is a possible by-product from the slag. A requirement for slags to be suitable for V extraction is a V content preferably above 8 wt% as V 2 O 3 and a phosphorus (P) content below 0.1 wt% as P 2 O 5 . Hence, it is important to keep V in the slag phase while the P is moved to the metal phase during the steelmaking process. The present research group has carried out parallel works to increase the understanding on how to concentrate V in the slag during steelmaking, while reaching a low P content. The works have been a part of the HYBRIT research program, a joint venture between the iron ore producer LKAB, steel producer SSAB and electricity producer Vattenfall, with the aim to pioneer fossil-free steel production. The starting point of the raw material has therefore been the existing high quality LKAB iron ore pellet named KPRS, designed for direct reduction (DR) shaft furnace technology. The composition of KPRS pellets can be seen in Table 1.

Materials Science