Simultaneous Recovery of Iron-Based Alloy and Production of Vanadium-Enriched Slag via Silicothermic Reduction of Chromium-Bearing Vanadium Slag

Lingxi Zhang,Min Chen

DOI: https://doi.org/10.1007/s11837-022-05612-6

2022-12-14

JOM

Abstract:The traditional roasting–leaching–calcining processes of chromium-bearing vanadium slag (CVS) to produce iron–vanadium alloys cause hazardous wastewater and high production costs. Sustainable and cost-efficient reduction technology has attracted much attention to shorten production procedures and control costs. The secondary resource solar-grade silicon cutting waste (Si-CW), as a strong reducing agent, is a solid waste generated during wafer slicing for solar cells. In this study, the enrichment/removal behaviors of CVS were investigated via thermodynamics and high-temperature experiments, to achieve the simultaneous production of an iron-based alloy and the preparation of vanadium-enriched slag using Si-CW as a reductant. Additionally, the reduction behaviors of iron, chromium, and vanadium oxides during the reduction process are discussed, and the reduction mechanism and reduction rate-controlling step are clarified and reviewed in detail. The results show that the maximum reduction degrees of FeO, Cr 2 O 3 , and MnO reach 92.5%, 65.2%, and 72.5%, respectively, at a temperature of 1873 K, a slag basicity of 0.75, and a Si-CW/CVS mass rate of 0.20. Vanadium-enriched slag with 15.36 wt.% V 2 O 3 has been successfully prepared, and the iron-based alloy product with 78.48 wt.% Fe, 5.32 wt.% Cr, and 16.20 wt.% Mn concentration was simultaneously produced.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy