RSC_CC_C1CC15595D 1..3

Hasigaowa Guan,Xi Wang,Shimou Chen,Y. Bando,D. Golberg

2011-01-01

Abstract:Silicon has long been regarded as one of the most promising next-generation anodes because of its highest known capacity (4200 mA h g ). However, a huge volume variation (B300%) during Li insertion–deinsertion causes pulverization of electrodes and thus rapid capacity fading. To tackle this issue, several approaches have been tried to fabricate various Si-based nanostructures. The capacity retention of these materials has indeed been significantly enhanced, but their rate capacities (which are highly required for electric vehicles) have only been marginally improved. In theory, the use of nanomaterials can improve the rate performance because of their short diffusion lengths; in practice, they must be elaborated into film electrodes which may negate the initial gains in diffusion length and electronic conductivity due to nanostructures, and even add supplementary interfaces between active materials. To resolve these problems, coaxial hybrid arrays, including active materialcore/conductive material-shell (type I) and conductive material-core/active material-shell (type II), seem to be a decent choice. For example, Liu et al. have reported the synthesis of ZnO@C nanorod arrays by a simple carbonization of pre-adsorbed glucose on ZnO arrays. Ajayan and coworkers have recently prepared novel CNT@MnO2 hybrid coaxial nanotubes via a template-mediated route. The carbon structures on either the shell or the core in these hybrids not only improve the conductivity but also act as a structural buffer, resulting in significantly improved electrochemical performance. Although being quite attractive, these two types of nanoarchitectured electrodes still have some structural limitations (see Fig. S1, ESIw), such as easy rupture of active nanostructures in the core for type I, and a relatively large electron length (Le) for type II. Herein, we present a new concept for fabrication of novel triple-layered array electrodes made of Cu nanopillar cores (robust conductive material), sandwiched amorphous Si layers (active one) and thin carbon shells (elastic conductive material). Both the inner robust Cu core and the outer elastic carbon layer not only prevent the electrodes from a mechanical breakage during the Si volume changes, but also provide continuous conductive paths in sandwiched Si layers, thus leading to significantly enhanced cycling stability and rate capability. The coaxial arrays have been fabricated by a combination of simple electrodeposition and chemical vapor deposition (CVD) techniques using a template, as shown in Fig. 1a. A layer of Pt film (B100 nm) was first sputtered onto one side of the commercially available AAO template which serves as the current collector for the electrode. Cu nanorod arrays were easily synthesized by electrodeposition inside the channels of AAO