Abstract:Mechanically robust alginate-based nanofibrous scaffolds were successfully fabricated by electrospinning method to mimic the natural extracellular matrix structure which benefits development and regeneration of tissues. Alginate-based nanofibres were electrospun from an alginate/poly(vinyl alcohol) (PVA) polyelectrolyte complex. SEM images revealed the spinnability of the complex composite nanofibrous scaffolds, showing randomly oriented, ultrafine, and virtually defects-free alginate-based/MgO nanofibrous scaffolds. Here, it is shown that an alginate/PVA complex scaffold, blended with near-spherical MgO nanoparticles (⌀ 45 nm) at a predetermined concentration (10% (w/w)), is electrospinnable to produce a complex composite nanofibrous scaffold with enhanced mechanical stability. For the comparison purpose, chemically cross-linked electrospun alginate-based scaffolds were also fabricated. Tensile test to rupture revealed the significant differences in the tensile strength and elastic modulus among the alginate scaffolds, alginate/MgO scaffolds, and cross-linked alginate scaffolds (P<0.05). In contrast to cross-linked alginate scaffolds, alginate/MgO scaffolds yielded the highest tensile strength and elastic modulus while preserving the interfibre porosity of the scaffolds. According to the thermogravimetric analysis, MgO reinforced alginate nanofibrous scaffolds exhibited improved thermal stability. These novel alginate-based/MgO scaffolds are economical and versatile and may be further optimised for use as extracellular matrix substitutes for repair and regeneration of tissues.

Sodium alginate/cellulose nanocrystal fibers with enhanced mechanical strength prepared by wet spinning

Toughen and strengthen alginate fiber by incorporation of polyethylene glycol grafted cellulose nanocrystals

Alginate/graphene oxide fibers with enhanced mechanical strength prepared by wet spinning

Aqueous-Based Coaxial Electrospinning of Genetically Engineered Silk Elastin Core-Shell Nanofibers

Potential of alginate fibers incorporated with drug-loaded nanocapsules as drug delivery systems

High-strength alginate fibers wet-spun from pre-crosslinked sodium alginate solutions

Fabrication and Characterization of Alginate Fibers by Wet-Spinning

High strength chitin nanocrystal/alginate filament prepared by wet-spinning in "green" coagulating bath

In Situ Modification of Alginate Fibers by Nano-montmorillonite for Enhancing the Mechanical Properties

Preparation and Properties of Nano-Silica/Calcium Alginate Blend Fibers

Preparation, Structure and Properties of High Strength Alginate Fiber

Constructing Stiff β-Sheet for Self-Reinforced Alginate Fibers

Hierarchical nano-helix as a new reinforcing unit for simultaneously ultra-strong and super-tough alginate fibers

Preparation of Hollow Calcium Alginate Microfiber Composited with Silicon Dioxide

High-Strength Regenerated Cellulose Fiber Reinforced with Cellulose Nanofibril and Nanosilica

Cellulose Nanofibrils/Alginates Double-Network Composites: Effects of Interfibrillar Interaction and G/M Ratio of Alginates on Mechanical Performance

Magnesium Oxide Nanoparticles Reinforced Electrospun Alginate-Based Nanofibrous Scaffolds with Improved Physical Properties

Dual roles of sodium polyacrylate in alginate fiber wet-spinning: Modify the solution rheology and strengthen the fiber

High mechanical performance based on the alignment of cellulose nanocrystal/chitosan composite filaments through continuous coaxial wet spinning

High-strength and functional nanocellulose filaments made by direct wet spinning from low concentration suspensions

Characterization and Functional Assessment of Alginate Fibers Prepared by Metal-Calcium Ion Complex Coagulation Bath.