Abstract:Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at $720 ^\circ$C and oxygen pressure $p_{O_2}=1-25 $Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO$_2$ as a secondary phase could be avoided for $p_{O_2}\ge 8 $Pa. However, transmission electron microscopy shows the presence of CeO$_2$ nanoclusters, even in those films which appear to be single phase in XRD. With O$_2$ annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La$_{0.7}$Ce$_{0.3}$MnO$_3$ with mixed Mn$^{3+}$/Mn$^{2+}$ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn$^{3+}$ and Mn$^{4+}$, and only a small amount of Mn$^{2+}$ ions can be observed by XAS. Mn$^{2+}$ and Ce$^{4+}$ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.

Magnetic properties and transport of epitaxial La0.47Ce0.20Ca0.33MnO3−δ films

Effects of oxygen content on the transport property of La0.7Ce0.3MnO3+δ film

Transport and Magnetic properties of laser ablated La0.7Ce0.3MnO3 films on LaAlO3: Effect of oxygen pressure, sample thickness and co-doping with Ca

Transport Properties and Mechanisms Modulated by Doping Ratio of Ce in La1-xCexMnO3 Electronic-doped Films

Transport and magnetic properties of La0.8Ce0.2MnO3 thin films grown by pulsed laser deposition

Phase Separation and Enhanced Magnetoresistance in the Strained Epitaxial La0.625ca0.375mno3 (001) Films

Magnetic and Transport Properties of Epitaxial (laba)co2o5.5+δ Thin Films on (001) SrTiO3

Magnetotransport Properties in La1−xCaxMnO3 (x=0.33, 0.5) Thin Films Deposited on Different Substrates

Study on magnetic properties for La0.67Sr0.33MnO3 − δ/Pr0.7Ca0.3MnO3 − δ/La0.67Sr0.33MnO3 − δ trilayer epitaxial film

Transport properties and laser-induced effect of the La0.5Sr0.5MnO3 film

Microstructure, Colossal Magnetoresistance Effect and Thermal Infrared Property of Annealed La0.7Sr0.3MnO3−δ Thin Films on Si(100)

Transport, magnetic, and structural properties of La$_{0.7}$Ce$_{0.3}$MnO$_3$ thin films. Evidence for hole-doping

Transport Properties and Laser-Indued Effect of the La0.5Sr0.5MnO3 Film

The synthesis and magnetoresistance behavior of direct current magnetron sputtering thin film of La0.7Pb0.3MnO3-δ

Oxygen In-Diffusion at Room Temperature in Epitaxial La0.7Ca0.3MnO3−δthin Films

Epitaxial Growth and Magnetic/transport Properties of La0.7Sr0.3MnO3 Thin Films Grown on SrTiO3 with Optimized Growth Conditions

Magnetic and Electrical Transport Properties of Er2o3-Doped La0.7ca0.3mno3 Composites

The Demonstration of Epitaxial and Electronic–magnetic Properties for La0.67Sr0.33MnO3−δ Films with (1 1 1) Orientation

The Effect of A-site Substitution of Ce and La on the Magnetic and Electronic Properties of Sr(Ti0.6Fe0.4)O(3-δ) Films.

Transport and magnetic properties in La0.7Ca0.3Mn1-xCuxO3

Anisotropic Magnetoresistance in Epitaxial La0.67(Ca1−xSrx)0.33MnO3 Films