La and S Co‐Doping Induced the Synergism of Multiphase Nickel‐Iron Nanosheets with Rich Oxygen Vacancies to Trigger Large‐Current‐Density Oxygen Evolution and Urea Oxidation Reactions
Yonghao Gan,Ying Ye,Xiaoping Dai,Xueli Yin,Yihua Cao,Run Cai,Bo Feng,Qi Wang,Xin Zhang
DOI: https://doi.org/10.1002/smll.202303250
IF: 13.3
2023-07-19
Small
Abstract:La and S co‐doping can induce the formation of multiphase, which further promotes the generation of NiOOH and rich oxygen vacancies. Beyond, La and S co‐doping can increase active sites, promote charge transfer, optimize the Gibbs free energy, and trigger the redox reactions of iron and lattice oxygen in FeOOH. The development of cost‐effective electrocatalysts for oxygen evolution reaction (OER) and urea oxidation reaction (UOR) is of great significance for hydrogen production. Herein, La and S co‐doped multiphase electrocatalyst (LSFN‐63) is fabricated by metal‐corrosion process. FeOOH can reduce the formation energy of NiOOH, and enhance the stability of NiOOH as active sites for OER/UOR. The rich oxygen vacancies can increase the number of active sites, optimize the adsorption of intermediates, and improve electrical conductivity. Beyond, La and S co‐doping can also regulate the electronic structure of FeOOH. As a result, LSFN‐63 presents a low overpotential of 210/450 mV at 100/1000 mA cm−2, small Tafel slope (32 mV dec−1), and outstanding stability under 1000 mA cm−2@60 h, and can also display excellent OER activity with 180 mV at 250 mA cm−2 and long‐term catalytic durability at 250 mA cm−2@135 h in 30 wt% KOH under 60 °C. Moreover, LSFN‐63 demonstrates remarkable UOR performance in 1 m KOH + 0.5 m urea, which just requires an ultra‐small overpotential of 140 mV at 100 mA cm−2, and maintain long‐term durability over 120 h. This work opens up a promising avenue for the development of high‐efficiency electrocatalysts by a facile metal‐corrosion strategy.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology