Abstract:As one of the most efficient, low-cost, and readily available electrocatalysts for oxygen evolution reaction (OER) in alkaline environments, the nickel-iron electrocatalyst is of great significance to commercial water splitting. In this study, NiFe-layered double hydroxide loaded on nickel foam (NiFe-LDH/NF) was synthe-sized via a simple one-step hydrothermal method, whose OER catalytic performance could be successfully optimized by further electrochemical reconstruction. The results show that NF is an effective precursor to loading crystallized Ni(OH)2 nanoparticles during hydrothermal synthesis, leading to the generation of high-performance NiOOH during OER reconstruction. Under the optimal Ni:Fe feeding ratio, Ni2Fe1-LDH/NF requires an ultra-low OER overpotential of 239 mV at 50 mA cm-2 and 260 mV at 100 mA cm-2 , whose Tafel slope is only 64.1 mV dec-1. Impressively, Ni2Fe1-LDH/NF also achieves an ultra-low voltage of 1.44 V at 10 mA cm-2 with excellent long-term stability for overall water splitting. Unlike the previous viewpoint that only Ni species dominate surface reconstruction of NiFe-LDH, in this article the decisive influence related to Fe species on the reconstruction layers' activity and stability is confirmed by electrochemistry, Raman, and XPS analysis during reconstruction process. During OER reconstruction, the surface Ni:Fe ratios can be "self -adaptively" regulated to an appropriate region, thus the stable reconstruction layers rich in NiOOH can be formed as the protective shells for NiFe-LDH. Furthermore, such "self-adaptive" reconstruction, assisted with appropriate initial Ni:Fe feeding ratios, can also stimulate more Ni3+ active sites for OER, benefitting the outstanding catalytic performance of NiFe-LDH/NF for overall water splitting and prospective large-scale application.(c) 2022 Elsevier B.V. All rights reserved.

Synergistic Effects in LaNiO3 Perovskites between Nickel and Iron Heterostructures for Improving Durability in Oxygen Evolution Reaction for AEMWE

Synergistic Effects in LaNiO3 Perovskites between Nickel and Iron Heterostructures for Improving Durability in Oxygen Evolution Reaction for AEMWE (Small Methods 9/2024)

Self-adaptively Electrochemical Reconstruction of NiFe-layered Double Hydroxide on Ni Foam for High-Performance Water Splitting

Multiple oxyanions modification on nickel–iron layered double hydroxides for enhanced oxygen evolution reaction

Boosting Oxygen Evolution Reaction of (Fe,Ni)Ooh via Defect Engineering for Anion Exchange Membrane Water Electrolysis Under Industrial Conditions

Interfacial electronic regulation on NiCo2O4 nanowires@NiFe-LDH nanosheets heterostructure for efficient oxygen evolution

Oxygen-vacancy-mediated electron localization at the nickel sites in nickel/iron layered double hydroxide towards efficient oxygen evolution reaction

Lanthanum‐Nickel‐Based Mixed‐Oxide‐Coated Nickel Electrodes for the OER Electrocatalysis

Enhanced Oxygen Evolution Reaction Activity of Fe-Doped Lithium Nickel-Based Metal Oxide through Modification of Nickel Oxidation State

Reinforced layered double hydroxide oxygen evolution electrocatalysts: polyoxometallic acid wet‐etching approach and synergistic mechanism

Engineering Lattice Oxygen Regeneration of NiFe Layered Double Hydroxide Enhances Oxygen Evolution Catalysis Durability

Iron and Nickel Mixed Oxides Derived From NiIIFeII-PBA for Oxygen Evolution Electrocatalysis

Iron-promoted Rapid Self-Reconstruction of Nickel-Based Catalysts for Efficient Oxygen Evolution

Exciting Lattice Oxygen of Nickel–iron Bi-Metal Alkoxide for Efficient Electrochemical Oxygen Evolution Reaction

Interface engineered NiFe2O4−x/NiMoO4 nanowire arrays for electrochemical oxygen evolution

Superlattice-Like Co-Doped Mn Oxide and NiFe Hydroxide Nanosheets toward an Energetic Oxygen Evolution Reaction

Optimizing the stability of NiFeOOH via oxyanion intercalation for water oxidation at large current densities

Novel Large-scale Integrated Non-Precious Metal Electrodes for Efficient and Stable Oxygen Evolution Reaction at High Current Density in 2.5 Kw Anion Exchange Membrane Water Electrolysis

Enhancing the Bifunctional Catalytic Performance of Porous La0.9Mn0.6Ni0.4O3- Nanofibers for Li-O2 Batteries Through Exsolution of Ni Nanoparticles

Accelerated Oxygen Evolution Kinetics by Engineering Heterojunction Coupling of Amorphous NiFe Hydr(oxy)oxide Nanosheet Arrays on Self‐Supporting Ni‐MOFs

Amorphous Nickel–Iron Borophosphate for a Robust and Efficient Oxygen Evolution Reaction