Role of Cerium on the Intricacies of Deformed State and Softening Mechanisms of Low‐Carbon Steels

Chetan Kadgaye,Md. Sameer Ansari,Sk. Md. Hasan,Sudipta Patra,Sumeer Kumar Nath,Anish Karmakar
DOI: https://doi.org/10.1002/srin.202300291
IF: 2.1258
2024-01-06
steel research international
Abstract:Two Cerium (Ce) added steels designated as low Ce (LCe) (0.03 wt% Ce) and high Ce (HCe) (0.6 wt% Ce) are 60% cold rolled and subcritically annealed at 600 °C, for 2‐16 h. During annealing, the influence of Ce, its precipitates (Ce2O3, Ce2O2S, and CeO2), and intermetallics (Ce2Fe17 and Ce2C3) on the softening mechanisms of above mentioned steels have been investigated. The present study investigates the softening kinetics of two cerium (Ce)‐modified steels after 60% cold rolling and annealing at 600 °C for 2–16 h. Cold rolling accumulates substantial strain in the ferritic matrix of low Ce (LCe) steel (0.03 wt% Ce) compared to high Ce (HCe) steel (0.6 wt% Ce). The acicular ferrite and Fe3C partition the imposed strain preferentially inside the ferrite matrix of LCe sample. Contrarily, a homogenous strain distribution in HCe sample is promoted by soft Ce2O3 particles embedded in ferrite. Both the steels achieve partial recovery and recrystallization even after 16 h of annealing. LCe steel experiences a softening fraction of ≈28 vol% after 16 h, inferior to HCe steel (≈34 vol%). During initial stage of annealing, nucleation of strain‐free grains are observed in LCe sample due to availability of grain and interphase boundaries. Subsequently, recrystallization kinetics get delayed because of the pinning effect exerted by fine CeO2 and Fe3C particles. In HCe samples, the early stage of ferrite nucleation is hindered by the segregation of Ce at grain boundaries. However, at a later stage, the recrystallization kinetics are accelerated owing to the ineffective pinning of dislocations and boundaries by coarse Ce2Fe17 and Ce2C3 particles.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?