Heteroatom-Doped Graphitic Carbon Nitrides for Reducing the Fire Hazard of Polystyrene
Chao Li,Juncheng Jiang,Lanjuan Xu,Lei Ni,Xinlei Jia
DOI: https://doi.org/10.1021/acsanm.4c00862
IF: 6.14
2024-01-01
ACS Applied Nano Materials
Abstract:High fire hazard, including heat release and toxic volatile production, has been the bottleneck in expanding the application of polystyrene (PS). Here, a heteroatom doping strategy is adopted to strengthen the flame-retardant effect of graphitic carbon nitride (g-C3N4) on PS. It is observed that the doped g-C3N4 fillers (PCN-1, PCN-2, PCN-3, BCN-1, BCN-2, BCN-3, PBCN-1, PBCN-2, and PBCN-3) show nanosheet-like morphologies, while common g-C3N4 presents bulky morphology. Also, the doped g-C3N4 fillers show higher thermal stability than common g-C3N4. Consequently, the doped g-C3N4 fillers show a better dispersion state in the PS matrix, benefiting the generation of an efficient barrier network. Cone results reveal that using the doped g-C3N4 fillers endows the polymer with a lower peak heat release rate, a peak smoke production rate, and a peak CO yield (PCOY). Typically, adding CN results in corresponding reductions of 7.2, 3.74, and 12.4%, respectively. By contrast, incorporating PCN-2 leads to decreases of 39.9, 23.0, and 53.2%, respectively. Thermogravimetric analysis/infrared spectrometry analysis indicates that the use of these additives contributes to the inhibition of the release of decomposed volatiles. Thus, it is firmly believed that utilizing heteroatom-doped g-C3N4 impairs the fire hazard of the polymer.