Abstract:Iron‐based pyrophosphate (Na4−αFe2+α/2(P2O7)2) is an attractive cathode for sodium‐ion batteries due to its cost‐effectiveness, feasible channels, and high operation voltage. Extending the solid solution range of Na4−αFe2+α/2(P2O7)2 enables generation of a novel off‐stoichiometric phase. Structural resolution, theoretical calculations, and sodium storage performance are comprehensively studied to disclose its structure–property relationship in sodium‐ion batteries. Iron‐based pyrophosphates are attractive cathodes for sodium‐ion batteries due to their large framework, cost‐effectiveness, and high energy density. However, the understanding of the crystal structure is scarce and only a limited candidates have been reported so far. In this work, we found for the first time that a continuous solid solution, Na4−αFe2+α/2(P2O7)2 (0 ≤ α ≤ 1, could be obtained by mutual substitution of cations at center‐symmetric Na3 and Na4 sites while keeping the crystal building blocks of anionic P2O7 unchanged. In particular, a novel off‐stoichiometric Na3Fe2.5(P2O7)2 is thus proposed, and its structure, energy storage mechanism, and electrochemical performance are extensively investigated to unveil the structure–function relationship. The as‐prepared off‐stoichiometric electrode delivers appealing performance with a reversible discharge capacity of 83 mAh g−1, a working voltage of 2.9 V (vs. Na+/Na), the retention of 89.2% of the initial capacity after 500 cycles, and enhanced rate capability of 51 mAh g−1 at a current density of 1600 mA g−1. This research shows that sodium ferric pyrophosphate could form extended solid solution composition and promising phase is concealed in the range of Na4−αFe2+α/2(P2O7)2, offering more chances for exploration of new cathode materials for the construction of high‐performance SIBs.

Sodium-Rich Ferric Pyrophosphate Cathode for Stationary Room-Temperature Sodium-Ion Batteries

Na2Fe(SO4)(2): an anhydrous 3.6 V, low-cost and good-safety cathode for a rechargeable sodium-ion battery

Activating the Inert Na1 Sites in Na<sub>2</sub>FePO<sub>4</sub>F Toward High Performance Sodium Storage

Carbon-Coated Na3.32 Fe2.34 (P2 O7 )2 Cathode Material for High-Rate and Long-Life Sodium-Ion Batteries

A New Polyanion Na3fe2(Po4)P2o7 Cathode With High Electrochemical Performance For Sodium-Ion Batteries

A New Polyanion Na 3 Fe 2 (PO 4 )P 2 O 7 Cathode with High Electrochemical Performance for Sodium-Ion Batteries

Zero-strain Co-doped Na2FeP2O7/carbon Delivers Superior Rate Capability and Long-Cycle Stability for Sodium Ion Batteries

Extending the solid solution range of sodium ferric pyrophosphate: Off‐stoichiometric Na3Fe2.5(P2O7)2 as a novel cathode for sodium‐ion batteries

Dual-strategy of carbon-coating and nanoengineering enables reversible and durable Na storage in an iron-based pyrophosphate cathode

A Green and Scalable Synthesis of Na 3 Fe 2 (PO 4 )P 2 O 7 /rGO Cathode for High‐Rate and Long‐Life Sodium‐Ion Batteries

Carbon-coated single crystal O3-NaFeO2 nanoflakes prepared via topochemical reaction for sodium-ion batteries

Highly Stable Na3Fe2(PO4)3@Hard Carbon Sodium-Ion Full Cell for Low-Cost Energy Storage

Unlocking Fast and Highly Reversible Sodium Storage in Fe-Based Mixed Polyanion Cathodes for Low-Cost and High-Performance Sodium-Ion Batteries

High-rate sodium storage performance enabled using hollow Co3O4 nanoparticles anchored in porous carbon nanofibers anode

Robust NASICON-type iron-based Na4Fe3(PO4)2(P2O7) cathode for high temperature sodium-ion batteries

Rapid mechanochemical synthesis of high-performance Na4Fe2.94Al0.04(PO4)2(P2O7)/C cathode material for sodium-ion storage

Sodium Iron Pyrophosphate: A Novel 3.0 V Iron-Based Cathode for Sodium-Ion Batteries

Dual‐Carbon‐Coated Na2FeP2O7 Cathode Materials for Na‐Ion Batteries with Superior High‐Rate and Cycling Stability

Fe 2 VO 4 Nanoparticles Anchored on Ordered Mesoporous Carbon with Pseudocapacitive Behaviors for Efficient Sodium Storage

Hollow-Sphere-Structured Na4Fe3(PO4)2(P2O7)/C As a Cathode Material for Sodium-Ion Batteries.

Unlocking iron-based mixed-phosphate cathode for sodium-ion batteries through off-stoichiometry