Ni 3 S 2 Nanoparticles Anchored on d-Ti 3 C 2 Nanosheets with Enhanced Sodium Storage
Chenyang Li,Dongdong Zhang,Jin Cao,Pengfei Yu,Jiaqian Qin,Xinyu Zhang
DOI: https://doi.org/10.1021/acsaem.0c03169
IF: 6.4
2021-02-25
ACS Applied Energy Materials
Abstract:To enhance structural stability and explore energy storage mechanisms for sodium-ion batteries, Ni<sub>3</sub>S<sub>2</sub> nanoparticles anchored on d-Ti<sub>3</sub>C<sub>2</sub> nanosheets (Ni<sub>3</sub>S<sub>2</sub>/d-Ti<sub>3</sub>C<sub>2</sub>) are designed and synthesized through the hydrothermal method followed by sulfurization reaction. Ni<sub>3</sub>S<sub>2</sub>/d-Ti<sub>3</sub>C<sub>2</sub> provides abundant active sites and reduces the Na<sup>+</sup> diffusion path, leading to high sodium storage performance. The d-Ti<sub>3</sub>C<sub>2</sub> nanosheets work as a conductive framework, providing high ion- and electron-conductive pathways and buffer volume change in Ni<sub>3</sub>S<sub>2</sub> nanoparticles, while Ni<sub>3</sub>S<sub>2</sub> nanoparticles exhibit high sodium storage and are applied as the spacer to suppress the restacking of d-Ti<sub>3</sub>C<sub>2</sub> nanosheets. The synergistic effect effectively improves sodium storage performance of the obtained electrode and shows a special capacitive and diffusive dual-model energy storage mechanism for sodium-ion batteries. Specifically, Ni<sub>3</sub>S<sub>2</sub> nanoparticles are battery-type components with high capacity, and the d-Ti<sub>3</sub>C<sub>2</sub> nanosheets are pseudocapacitive components with a high pseudocapacitive value and fast energy storage. Consequently, the Ni<sub>3</sub>S<sub>2</sub>/d-Ti<sub>3</sub>C<sub>2</sub> electrode provides enhanced performance (234.4 mA h g<sup>–1</sup> at 0.1A g<sup>–1</sup>), almost 5.5 times that of the d-Ti<sub>3</sub>C<sub>2</sub> electrode (∼42.4 mA h g<sup>–1</sup>). The results show that this metal sulfide incorporation strategy presents a prospective way to heighten sodium storage performance of d-Ti<sub>3</sub>C<sub>2</sub> MXene.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c03169?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c03169</a>.Experimental and calculation section; figures showing XRD, SEM, and TEM results of the precursors; XRD of Ni<sub>3</sub>S<sub>2</sub>; sodium storage performance of comparative groups; CV curves at various scan rates of d-Ti<sub>3</sub>C<sub>2</sub> and Ni<sub>3</sub>S<sub>2</sub>; GITT of Ni<sub>3</sub>S<sub>2</sub>/d-Ti<sub>3</sub>C<sub>2</sub>; and SEM and TEM images after cycling (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c03169/suppl_file/ae0c03169_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels