Carbon-Coated Tin-Titanate derived SnO2/TiO2 nanowires as High-Performance anode for Lithium-Ion batteries
Qianjiao Ge,Zhenhan Ma,Menglong Yao,Hao Dong,Xinyang Chen,Shiqi Chen,Tianhao Yao,Xin Ji,Li Li,Hongkang Wang
DOI: https://doi.org/10.1016/j.jcis.2024.02.015
IF: 9.9
2024-05-01
Journal of Colloid and Interface Science
Abstract:Tin dioxide (SnO<sub>2</sub>) is a promising alternative material to graphite anode, but the large volume change induced electrode pulverization issue has limited its application in lithium-ion batteries (LIBs). In contrast, titanium dioxide (TiO<sub>2</sub>) anode shows high structure stability upon lithium insertion/extraction, but with low specific capacity. To overcome their inherent disadvantages, combination of SnO<sub>2</sub> with TiO<sub>2</sub> and highly conductive carbon material is an effective way. Herein, we report a facile fabrication method of carbon-coated SnO<sub>2</sub>/TiO<sub>2</sub> nanowires (SnO<sub>2</sub>/TiO<sub>2</sub>@C) using tin titanate nanowires as precursor, which are prepared by reacting SnCl<sub>2</sub>·2H<sub>2</sub>O with layered sodium titanate (Na<sub>2</sub>Ti<sub>3</sub>O<sub>7</sub>) nanowires in the aqueous solution though the ion exchange between Sn<sup>2+</sup> and Na<sup>+</sup>. After annealing under argon atmosphere, the hydrothermally carbon-coated tin-titanate nanowires decompose, forming a unique hybrid structure, where ultrafine SnO<sub>2</sub> nanoparticles are uniformly embedded within the TiO<sub>2</sub> substrate with carbon coating. Consequently, the SnO<sub>2</sub>/TiO<sub>2</sub>@C nanowires demonstrate excellent lithium storage capacity with high pseudocapacitance contribution, excellent reversible capacity, and long-term cycling stability (673.7/510.5 mAh/g at 0.5/1.0 A/g after 250/800 cycles), owing to the unique hybrid structure, as the well-dispersion of ultra-small SnO<sub>2</sub> within TiO<sub>2</sub> nanowire substrate with simultaneous carbon coating efficiently suppresses the volume changes of SnO<sub>2</sub>, provides abundant reactive sites for lithium storage, and enhances the electrical conductivity with shortened ion transport distance.
chemistry, physical