Multifunctional magnesium organic framework-based photothermal and pH dual-responsive mouthguard for caries prevention and tooth self-healing promotion

Qun Li,Jinbiao Liu,Huijie Liu,Yue Sun,Yingying Xu,Kexin Wang,Wenjing Huang,Lan Liao,Xiaolei Wang

DOI: https://doi.org/10.1016/j.bioactmat.2023.06.017

IF: 18.9

2023-07-01

Bioactive Materials

Abstract:Highlights • A new foam mouthguard of convenient operation and precise anti-bacteria was proposed for caries prevention and tooth self-healing promotion. Moreover, this versatile biomedical material can prevent caries from three aspects: the regulation of pH environment, the destruction of biofilm adhesion, and the inhibition of virulence gene expression. Caries is considered to be the most prevalent non-communicable disease in humans, mainly deriving from acidogenic bacterial biofilm and resulting in the demineralization and decomposition of hard dental tissue. Herein, a composite responsive foam brace loaded with magnesium organic framework (MPC) is designed for caries prevention and tooth remineralization. MPC can intelligently release organic antibacterial molecules (gallic acid) and mineralized ions (Mg 2+ , Ca 2+ and PO 4 3− ) under acidic conditions (pH < 5.5) of biofilm infection, regulating pH and killing bacteria. Additionally, due to the excellent photothermal conversion efficiency, MPC can further enhance the destruction of bacterial biofilm by inhibiting virulence genes and destroying bacterial adhesion under near-infrared light irradiation (808 nm). More importantly, MPC can not only reverse the cariogenic environment at both pH and microbial levels, but also promote self-healing of demineralized teeth in terms of both the micro-structure and mechanical properties. Graphical abstract Graph 1. Schematic illustration of construction of MPC and working principle. (a) The construction of MPC. (b) The usage of MPC. (c) Photothermal and pH dual-responsive MPC for localized biofilm disruption, oral microenvironment optimization and tooth hard tissue self-healing.As shown in Graph 1a, gallic acid, a natural gallnut component, was used as an organometallic framework to form magnesium-organic framework (Mg-MOF). Then poly-dopamine (PDA) with outstanding photothermal conversion efficiency was wrapped on the Mg-MOF. Finally, calcium phosphate (CaP) was loaded on the surface of by biomimetic mineralization to form composite nanomaterial @CaP (MPC). To facilitate the application of this system, MPC-CB foam braces were formed by loading with the foaming agent (cocamidopropyl betaine, Graph 1b). As shown in Graph 1c, caries caused pathophysiological pH fluctuations in the oral microenvironment that could trigger this intelligent nanosystem. Under acidic conditions generated by biofilm infection, the CaP coating of MPC degraded and released Ca 2+ and PO 4 3− , followed by the release of Mg 2+ and naturally active antimicrobial molecules (gallic acid) from the collapsed organic framework. In addition, the ability of biofilm destruction could be further improved under NIR irradiation. Meanwhile, the degradation of coating and frame could ameliorate the low pH situation of the lesion site and reverse the carious environment. Gallic acid and PDA had good affinity for inorganic components (calcium and phosphorus) and organic component (collagen) in tooth tissue, which could effectively stabilize tooth hard tissue. More importantly, the released Ca 2+ , PO 4 3− and Mg 2+ could promote the self-repair of teeth, and then restore the mechanical properties. Download : Download high-res image (380KB) Download : Download full-size image

engineering, biomedical,materials science, biomaterials