Abstract:A Co0.5Mn1Fe0.25Al0.75Ox-LDO catalyst was developed which showed excellent performance for the low-temperature NH3-SCR. NOx conversions ∼100% were achieved in the whole 100-250 °C range, while after 10-h operation at 150 °C with 100 ppm SO2/5 vol% H2O in the feed, the NOx conversion was maintained at 80%. This catalyst provided a much better N2-selectivity than the Mn1Fe0.25Al0.75Ox-LDO and Mn1Al1Ox-LDO, especially at 150-300 °C. It was found that Co0.5Mn1Fe0.25Al0.75Ox possessed higher surface acidity and reducibility, while XPS analyses indicated an electron transfer between Co3+/Co2+ and Mn4+/Mn3+ redox cycles, leading to a much lower N2O formation, supported by Density Functional Theory (DFT) calculations. Detailed analysis of gas responses obtained upon various step-gas switches was performed, which allowed to measure the surface concentration and reactivity of preadsorbed NOx-s and NHx-s leading to N2 and N2O. Transient kinetic and DFT studies strongly suggested likely mechanisms of NH3-SCR and the critical role of Co for N2-selectivity enhancement.

What problem does this paper attempt to address?

This paper primarily explores the application of cobalt (Co)-modified manganese-iron-aluminum layered double oxide (LDO) catalysts in the ammonia selective catalytic reduction (NH₃-SCR) reaction, particularly focusing on improving nitrogen (N₂) selectivity and reducing nitrous oxide (N₂O) formation. ### Research Background and Objectives - **Research Background**: Ammonia selective catalytic reduction (NH₃-SCR) is currently one of the most effective nitrogen oxides (NOₓ) control technologies, widely used in stationary sources (such as coal, oil, and natural gas power plants and industrial boilers) and mobile sources (such as heavy-duty diesel vehicles). Traditional industrial catalysts like V₂O₅-WO₃(MoO₃)/TiO₂ and Fe-ZSM-5 operate at higher temperatures but show decreased performance under low-temperature conditions and are easily affected by sulfur dioxide (SO₂), alkali metals, fly ash, and water vapor in the flue gas. - **Research Objectives**: Develop an NH₃-SCR catalyst that can effectively operate at lower temperatures (<250°C), with a particular focus on improving N₂ selectivity and reducing N₂O formation. ### Main Findings - **Catalyst Preparation**: Co-Mn-Fe-Al-NO₃ layered double hydroxides (LDH) with different cobalt contents were synthesized by co-precipitation, followed by calcination to convert them into LDO catalysts. - **Performance Improvement**: At a Co/Mn molar ratio of 0.5, the Co₀.₅Mn₁Fe₀.₂₅Al₀.₇₅Oₓ-LDO catalyst exhibited significantly enhanced N₂ selectivity in the 150-250°C range, especially with nearly 100% NOₓ conversion at low temperatures. Even after 10 hours of operation in an inlet stream containing 100ppm SO₂ and 5% H₂O, the NOₓ conversion rate remained around 80%. - **Mechanism Analysis**: Transient kinetic analysis and density functional theory (DFT) calculations revealed the mechanism by which Co improves N₂ selectivity. The study showed that the introduction of Co promotes electron transfer between Co³⁺/Co²⁺ and Mn⁴⁺/Mn³⁺, effectively inhibiting N₂O formation. Additionally, transient kinetic analysis provided critical information on the surface concentration and activity of pre-adsorbed NOₓ and NHₓ species, aiding in understanding the NH₃-SCR reaction pathway and the important role of Co in enhancing N₂ selectivity. In summary, this study developed a novel Co-modified LDO catalyst that not only improves the activity of the NH₃-SCR reaction under low-temperature conditions but also significantly enhances N₂ selectivity, providing a potential effective solution for industrial flue gas purification.

Remarkable N2-selectivity enhancement of practical NH3-SCR over Co0.5Mn1Fe0.25Al0.75Ox-LDO: The role of Co investigated by transient kinetic and DFT mechanistic studies

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Mechanistic Investigation of the Enhanced SO2 Resistance of Co-modified MnOx Catalyst for the Selective Catalytic Reduction of NOx by NH3

Synthesis of novel Co(3-x)MnxO4@TiO2 core-shell catalyst for low-temperature NH3-SCR of NOx with enhanced SO2 tolerance

Behavior and structure tuning of (Mn&Fe)AlOx-based catalysts for superior denitrification performance

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures

Interactions between CO oxidation and selective catalytic reduction of NO with NH3 over Mn-based catalysts

Mechanism of NO reduction by NH3 over MnCuOx catalysts and the influence mechanism of CO

Boosting Low-Temperature NH3-SCR Performance Via Mixed-Valence Cobalt Dual Active Sites

Optimization of catalytic activity of MnCoOx catalyst for NH3–SCR at low temperature by response surface method

Getting insight into the CO tolerance over Co-modified MnSm/Ti catalyst for NH 3 -SCR of NO x at low temperature: Experiments and DFT studies

Low-cost Co–Al spinel and M–Co–Al (M = Fe and Ce) catalysts for selective catalytic reduction of NOx with NH3

Simultaneously achieving selective catalytic reduction of NOx with NH3 and catalytic oxidation of CO with O2 over one finely optimized bifunctional catalyst Mn2Cu1Al1Ox at low temperatures

Tunable Highly Dispersed Nia-xMnxAlOy Catalysts Derived from Layered Double Oxide for Low Temperature NOx Removal

Abundant Oxygen Vacancies Induced by the Mechanochemical Process Boost the Low-Temperature Catalytic Performance of MnO2 in NH3-SCR

Efficient FeMn/Al2O3 catalyst for NH3-SCR of NO at low temperature: the Influence of Strong Interactions Between Active Components and Carrier

"Oxynitride trap" over N/S co-doped graphene-supported catalysts promoting low temperature NH3-SCR performance: Insight into the structure and mechanisms

One-step synthesis by redox co-precipitation method for low-dimensional Me-Mn bi-metal oxides (Me=Co, Ni, Sn) as SCR DeNOx catalysts

C,N ‐modified TiO 2 ‐supported Mn–Ce–Co x ‐based catalyst for low‐temperature NH 3 ‐SCR

Regulating the valence and size of the active center of Co/Al2O3 catalyst improved the performance and selectivity of NH3-SCO