Investigation on 3D fatigue crack propagation in pitch bearing raceway of offshore wind turbines

Yiming Chen,Xin Jin,Yong Yue,Shuang Wang,Huali Han,Maoshi Wen,Qingfeng Wang,Peng Cheng

DOI: https://doi.org/10.1016/j.oceaneng.2022.113524

IF: 5

2023-01-12

Ocean Engineering

Abstract:In complex marine environments, pitch bearings are more prone to crack initiation, propagation, and evolution, which leads to contact fatigue problems. Accurately identifying and predicting the evolution of early crack extensions in pitch bearings can effectively prevent major economic losses caused by failure. The two limitations of the current research on pitch bearing cracking are the low efficiency of the simulation and the fact that the contact fatigue models are mostly simplified to two-dimensional models. These models do not accurately reflect the influence of the raceway geometry parameters on the real situation. This study combined Bladed and MATLAB for an integrated life cycle simulation using Python and a cloud platform to reduce the simulation duration. A three-dimensional modelling method was proposed to calculate the crack propagation in pitch bearings throughout the full life cycle. The effects of different operating conditions, crack depths, and initial crack angles were investigated and analyzed. The results suggested that the maximum Hertz contact stress was 2961.4 MP. When the initial crack angle was greater than 0°, the crack generally propagated towards the core area. When the crack angle was less than 30°, the crack propagated gradually in depth and towards the surface. The fatigue life at an initial crack angle of 60° was 1.5 times that of an initial crack angle of 30°.

engineering, civil, ocean, marine,oceanography