Abstract:The failure of fiber-reinforced ceramic and metal matrix composites under a fixed load for extended times occurs because of strength degradation in the constituent fibers. Specifically, the ceramic fibers possess a Weibull strength distribution caused by crack-like flaws, which can grow according to a power-law growth mechanism. Failure of individual fibers causes interfacial slippage and stress redistribution to unfailed fibers, which in turn accelerates the degradation rate of the remaining fibers, and culminates in abrupt failure of the composite after sufficient damage has accumulated. This sequence of events is modeled both analytically and numerically within the Global Load Sharing (GLS) approximation previously utilized for quasi-static loading. Analytically, a general constitutive model for the relationship between the stress on the damaged fiber bundle, the strain in the unbroken fibers, and the extent of damage, is combined with a time-dependent damage evolution equation derived from the slow-crack-growth kinetics to yield an integral equation for the strain vs time at fixed applied load. The relevant gauge length for a fixed-load rupture process is found to be δ = rστ which is twice the slip length prevailing at the initial applied load σ, where τ is the interfacial sliding resistance between fiber and matrix. The underlying time scale for rupture is the time scale for a typical fiber of gauge length δ to fail under the applied load σ; this time can be quite different from that measured by stress-rupture tests on single fibers at an unrelated laboratory gauge length L0. A simple, accurate but approximate relationship between applied load, time to failure, fiber Weibull modulus, and slow crack growth exponent is presented. The numerical simulations of the same degradation process verify the general accuracy of the failure time obtained from the analytic results. The remaining tensile strength after some time at load but prior to failure is also studied, and the simulation results generally exhibited a more sudden-death failure than the analytical predictions. A specific application to the failure of a Nicalon fiber composite is presented.

Failure due to fatigue in fiber bundles and solids

Dynamic critical behavior of failure and plastic deformation in the random fiber bundle model

Failure properties of fiber bundle models

Precursors of catastrophe in the BTW, Manna and random fiber bundle models of failure

Material failure time and the fiber bundle model with thermal noise

Inequality of creep avalanches can predict imminent breakdown

From nucleation to percolation: the effect of system size when disorder and stress localization compete

Time dependent fracture under unloading in a fiber bundle model

Stability in fiber bundle model : Existence of strong links and the effect of disorder

Fatigue failure in glasses under cyclic shear deformation

Cracks in random brittle solids: From fiber bundles to continuum mechanics

Time-dependent failure in fiber-reinforced composites by fiber degradation

Avalanche shapes in fiber bundle model

Scaling behaviour in the fracture of fibrous materials

Failure process of fiber bundles with random misalignment

Scaling in the time-dependent failure of a fiber bundle with local load sharing

Effect of localized loading on failure threshold of fiber bundles

Avalanche shapes in the fiber bundle model

Maximizing the strength of fiber bundles under uniform loading

Energy bursts in fiber bundle models of composite materials

Universality behind Basquin's law of fatigue