Prominent cryogenic fluorescence temperature sensing and superior room-temperature photochromism in Bi/Eu codoped KNN transparent-ferroelectric ceramics

Ping Zhou,Qifa Lin,Xiangfu Zeng,Min Gao,Chunlin Zhao,Cong Lin,Tengfei Lin,Xiao Wu

DOI: https://doi.org/10.1016/j.jre.2024.11.007

IF: 4.632

2024-11-11

Journal of Rare Earths

Abstract:Highlights • Bi/Eu codoped KNN transparent-ferroelectric ceramics were prepared. • PL, PC behavior, temperature sensing and ferro-/piezoelectricity were integrated. • The S r value of 0.5Bi-1Eu-KNN reached 26.32%K -1 at ultralow temperature. • The PC contrast of 0.5Bi-1Eu-KNN is as high as 75.2% at room temperature. • I 614 / I 592 can serve as a reliable indicator for detecting the R-O phase transition. The growing demand for the miniaturization and multifunctionality of optoelectronic devices has promoted the development of transparent ferroelectrics. However, it is difficult for the superior multiple optical properties of these materials to be compatible with the excellent ferroelectricity and piezoelectricity in transparent ceramics. Here, we successfully synthesized Bi/Eu codoped eco-friendly K 0.5 Na 0.5 NbO 3 transparent-ferroelectric ceramics with photoluminescence (PL) behavior, photochromic (PC) reactions and temperature-responsive PL. Based on the distinct optical properties of ceramics at different temperature ranges (room temperature and ultralow temperature), high utilization of multiple optical functions was realized. At room temperature, the PC behavior induced PL modulation contrast reaches 75.2% (at 592 nm), which can be applied in the optical information storage field. In the ultralow temperature range, the ceramics exhibit excellent sensitivity (with a maximum relative sensitivity of 26.32%/K) via fluorescence intensity ratio technology and exhibit great application potential in noncontact optical temperature measurements. Additionally, the change in the PL intensity at different wavelengths ( I 614 / I 592 ) can serve as a reliable indicator for detecting the occurrence of the phase transition from rhombohedral to orthorhombic at low temperature. This work provides a feasible paradigm for realizing the integration of ferroelectricity and multifarious optical properties in a single optoelectronic material. Graphical abstract In this work, Bi/Eu codoped KNN ceramics were designed to induce the coexistence of orthorhombic and tetragonal phases with dense microstructure and small grain size, which not only improve the optical transparency and maintain moderate ferroelectricity, but also exhibit excellent PC behavior and fluorescence temperature sensing performance. Download: Download high-res image (178KB) Download: Download full-size image

chemistry, applied