Abstract:Objective: The present study determined the influence of polymerization shrinkage of eight commercially available hybrid, micro-filled and nano composites (Z100 and Filtek Supreme, 3M-ESPE; Charisma and Durafill, Heraeus Kulzer; Tetric and InTen-S, Ivoclar Vivadent; Enamel plus HFO, GDF; Palfique Estelite Low Flow, Tokuyama) placed in large class 1 cavities on the bond strength to dentin. Methods: Polymerization shrinkage was recorded for 300 s at room temperature with a Stress-Strain-Analyzer (C(FACTOR)=0.3). The maximum contraction stresses after 300 s, the time until gelation (t(0.5 N)) and the coefficient of near linear fit of contraction force/time (gradient) were analysed. For the evaluation of the micro-tensile-bond-strength (micro-TBS), hourglass shape samples obtained from a total of 32 no carious extracted human third and second molars, randomly divided into 8 groups, were used. Micro tensile bond strengths were determined by computing the ratio of maximum load by the adhesion area of the hourglass shape. In order to analyze the quality of the polymerization within fillings, hardness profiles of a surface cut thought the middle of the restored tooth and along the tooth axis were made. Further, the modulus of elasticity, determined in a three-point-bending test, as well as the variation of the modulus of elasticity and of the hardness within a filling were considered. The statistical analyses were conducted by ANOVA (alpha=0.05) and post-hoc Tukey's test. Results: A significant correlation between polymerization shrinkage and micro-TBS was found (Pearson; -0.44). The correlation between modulus of elasticity in bending test and shrinkage stress (Pearson; 0.77), coefficient of near linear fit m (Pearson; 0.72), time until gelation (Pearson; -0.52) and micro-tensile-bond-strength (Pearson; -0.45) was also significant. A high polymerization tension and modulus of elasticity negatively affected the adhesion of the composite to the tooth hard substance. Further, the number of samples lost during the slice cutting and the hourglass shape preparation was found to correlate highly significantly with the shrinkage stress (Pearson; 0.97), coefficient of near linear fit m (Pearson; 0.94) and modulus of elasticity (Pearson; 0.82). All materials showed sufficient polymerization within the filling in comparison to the filling surface, the hardness at the bottom of the filling was greater than 80% of the maximum hardness value. The modulus of elasticity was not considerably reduced within the filling. Significance: High contraction stress and modulus of elasticity, fast development of contraction force and an early start of stress build-up of materials placed in restrictive cavities cause tension in the material with a possible subsequent distortion of the bond to the tooth structure. A low modulus of elasticity is not necessarily associated with high bond strength. However, it causes a more uniform stress distribution at the restorative composite-tooth interface. This is also evident in a reduced sample loss during the different stages of sample preparation.

Evaluating flexure properties, hardness, roughness and microleakage of high-strength injectable dental composite: an in vitro study

Comparison of Flexural Strength and Wear of Injectable, Flowable and Paste Composite Resins

The mechanical, wear, antibacterial properties and biocompatibility of injectable restorative materials under wet challenge

Mechanical properties of combined packable and high-filled flowable composite used for the fixed retainer: an in vitro study

Flexural Properties, Wear Resistance, and Microstructural Analysis of Highly Filled Flowable Resin Composites.

Investigations on mechanical behaviour of dental composites

The Chemical and Optical Stability Evaluation of Injectable Restorative Materials Under Wet Challenge

Surface Properties and Color Stability of Dental Flowable Composites Influenced by Simulated Toothbrushing

Comparative analysis of self-cure and dual cure-dental composites on their physico-mechanical behaviour

Characterization of Contemporary Conventional, Bulk-fill, and Self-adhesive Resin Composite Materials

Physico-mechanical characteristics of commercially available bulk-fill composites

Influence of Filler Particle Sizes on the Physical Properties of Bulk-Fill Composites Compared to Conventional Composites

Flowable composite as an alternative to adhesive resin cement in bonding hybrid CAD/CAM materials: in-vitro study of micro-shear bond strength

Mechanical Properties of Bulk-Fill Resin Composites with Single Increment Up to 4 Mm: A Novel Mechanical Strength Test

Mechanical properties and fracture behavior of flowable fiber reinforced composite restorations

Comparison of mechanical properties of a new fiber reinforced composite and bulk filling composites

Evaluation of Mechanical Properties of Four Kinds of Composite Resins for Inlay

Wear and roughness analysis of two highly filled flowable composites

Correlation between Dental Composite Filler Percentage and Strength, Modulus, Shrinkage Stress, Translucency, Depth of Cure and Radiopacity

The antibacterial, cytotoxic, and flexural properties of a composite resin containing a quaternary ammonium monomer.

Evaluation of micro-tensile bond strengths of composite materials in comparison to their polymerization shrinkage