Effect of MOF-derived carbon–nitrogen nanosheets co-doped with nickel and titanium dioxide nanoparticles on hydrogen storage performance of MgH 2
Zhiqiang Lan,Feifan Hong,Weitao Shi,Ruolin Zhao,Renhuan Li,Yi Fan,Haizhen Liu,Wenzheng Zhou,Hua Ning,Jin Guo
DOI: https://doi.org/10.1016/j.cej.2023.143692
IF: 15.1
2023-05-27
Chemical Engineering Journal
Abstract:Magnesium hydride (MgH 2 ) is considered one of the most ideal materials for hydrogen storage. However, the practical applications of MgH 2 are greatly hindered by its high operating temperature and poor hydrogen storage kinetics. In the present work, carbon–nitrogen nanosheets co-doped with disk-like nickel and titanium dioxide nanoparticles ((Ni, TiO 2 )CN) were prepared using metal–organic frameworks (MOFs) as precursors to improve the hydrogen storage performance of MgH 2 . The as-synthesized ((Ni, TiO 2 )CN)-doped MgH 2 system manifested excellent hydrogen storage properties at low temperatures and could absorb 5.08 wt% of hydrogen in 100 min at 40 °C and 6.17 wt% of hydrogen in 10 min at 125 °C. The dehydrogenation activation energy of the ((Ni, TiO 2 )CN)-doped MgH 2 system was obtained as 83.1 kJ∙mol −1 , which was considerably lower than that of pure MgH 2 . The mechanism analysis revealed that Ni reacted with Mg to form Mg 2 Ni coating around Mg, the in situ Mg 2 Ni and its hydride (Mg 2 NiH 4 ) acted as a "hydrogen pump" to drive hydrogen diffusion and dissociation. And the mutual reversible change in polyvalent Ti ions could promote the transfer of charge, which was conducive to accelerating the formation of Mg/MgH 2 . Additionally, stable CN layers not only could inhibit the fragmentation and agglomeration of MgH 2 particles, but also could make the active substance dispersed more evenly; thus, the cycle stability and hydrogen absorption and desorption kinetics of MgH 2 was greatly enhanced under the synergistic catalysis of in situ formed Mg 2 Ni/Mg 2 NiH 4 , polyvalent titanium, and N-C nanosheets. The findings of this work could provide a new strategy to improve the properties of Mg-based hydrogen storage materials.
engineering, chemical, environmental