Highly active multivalent multielement catalysts derived from hierarchical porous TiNb 2 O 7 nanospheres for the reversible hydrogen storage of MgH 2

Lingchao Zhang,Ke Wang,Yongfeng Liu,Xin Zhang,Jianjiang Hu,Mingxia Gao,Hongge Pan

DOI: https://doi.org/10.1007/s12274-020-3058-4

IF: 9.9

2020-01-01

Nano Research

Abstract:Critical limitations in applying MgH 2 as a hydrogen-storage medium include the high H 2 desorption temperature and slow reaction kinetics. In this study, we synthesized hierarchical porous TiNb 2 O 7 spheres in micrometer scale built with 20–50 nm nanospheres, which showed stable activity to catalyze hydrogen storage in MgH 2 as precursors. The addition of 7 wt.% TiNb 2 O 7 in MgH 2 reduced the dehydrogenation onset temperature from 300 to 177 °C. At 250 °C, approximately 5.5 wt.% H 2 was rapidly released in 10 min. Hydrogen uptake was detected even at room temperature under 50 bar hydrogen; 4.5 wt.% H 2 was absorbed in 3 min at 150 °C, exhibiting a superior low-temperature hydrogenation performance. Moreover, nearly constant capacity was observed from the second cycle onward, demonstrating stable cyclability. During the ball milling and initial de/hydrogenation process, the high-valent Ti and Nb of TiNb 2 O 7 were reduced to the lower-valent species or even zero-valent metal, which in situ created multivalent multielement catalytic surroundings. A strong synergistic effect was obtained for hybrid oxides of Nb and Ti by density functional theory (DFT) calculations, which largely weakens the Mg-H bonding and results in a large reduction in kinetic barriers for hydrogen storage reactions of MgH 2 . Our findings may guide the further design and development of high-performance complex catalysts for the reversible hydrogen storage of hydrides.