Characterization of the oxide film and deuterium permeation behavior of CoCrMnFeNi high entropy alloy oxidized at 550 °C for 24 hours

Chunyu Yin,Wenxuan Li,Xi Qiu,Bin Luo,Hongtao Huang

DOI: https://doi.org/10.1016/j.matlet.2023.134632

IF: 3

2023-05-30

Materials Letters

Abstract:High entropy alloys have become potential candidate materials for high temperature nuclear reactor due to its high strength, high hardness, excellent corrosion resistance and radiation resistance, therefore the compatibility of hydrogen isotopes with HEAs becomes a key issue that has attracted a lot of attentions. The deuterium permeation behavior of the CoCrMnFeNi high entropy alloy after oxidation at 550 °C for 24 h was investigated by gas-phase deuterium permeation testing, SEM, X-ray diffraction methods in this paper. The results show that an oxide film with a thickness of about 1μm was formed on the surface of the sample after oxidation. The outer layer of the oxide film is rich in Mn 2 O 3 and the inner layer is rich in Cr 2 O 3 . The deuterium permeability of the CoCrMnFeNi sample after oxidation was reduced by an order of magnitude and was 1/7-1/17 times as high as that for the unoxidized one.

materials science, multidisciplinary,physics, applied