Abstract:Aim: To explore the degradation characteristics of composite of calcium polyphosphate fiber (CPPF), calcium phosphate cement (CPC) and micromorselized bone in vitro. Methods: The experiment was conducted in the Central Laboratory of Animal Experiment of the First Hospital Affiliated to Harbin Medical University from February to October 2005. 1 The rabbit iliac bone was made into micromorselized bone with the diameter of 300-500 μm. 2 Two groups of biochemical composite were made respectively according to the mass-ratios of CPPF/CPC/micromorselized bone at 1:4:4 (CPPF group/CPC group/micromorselized bone group) and that of CPC/micromorselized bone at 1:1 (CPC group/micromorselized bone group). 3 The porosity was calculated by studying the pore diameter of composite under scanning electron microscope. 4 In vitro experiment of degradation, two groups of composite were put into the phosphate buffered solution (PBS) (pH 7.4) respectively to study the changes in weight-loss ratio of composite in degradation liquid as well as the changes in pH value of degradation liquid and the biomechanical changes in composite at different time-points. Results: 1 Changes in porosity, pH value and mass of degradation of both kinds of composites: The porosity of composite of CPPF/CPC/ micromorselized bone was 72.1% with the pore diameter of 100-400, and the pH value was constant while degradation. The mass changed little within 4 weeks and decreased rapidly after the 4th week, which was 50% of the initial mass in the 12th week. The porosity of compound materials of CPC/micromorselized bone was 58.2% and was 50-300 μm in the gap diameter with slight changes in pH value, and the mass changed little within 6 weeks, which decreased rapidly after 6 week, and was 70% of the initial mass in the 12th week. 2 Biomechanical changes in composite of two groups in the degradation: the primary biomechanical strength was 9.28 MPa in CPPF/CPC/micromorselized bone and was 6.21 MPa in CPC/ micromorselized bone, and there was significant difference between them (P< 0.05). The strength of CPPF/CPC/micromorselized bone decreased slowly within 4 weeks, then decreased obviously after 4 weeks, which was 0.18 MPa in the 12th week, while the strength of CPC/micromorselized bone decreased symmetrically and was 0.24 MPa in the 12th week. Conclusion: The composite of CPPF/CPC/micromorselized bone is a new bone repair material, which is suitable for bone tissue engineering for its good characteristics of porosity, pore diameter and degradation.

The study on calcium polyphosphate/poly-amino acid composite for supportive bone substitute materials in vitro

In vitro study of the biphasic calcium phosphate/chitosan hybrid biomaterial scaffold fabricated via solvent casting and evaporation technique for bone regeneration

Preparation, characterization, and in vitro and in vivo biocompatibility evaluation of polymer (amino acid and glycolic acid)/hydroxyapatite composite for bone repair

Biological evaluation of the modified nano-amorphous phosphate calcium doped with citrate/poly-amino acid composite as a potential candidate for bone repair and reconstruction

Developing novel Ca-zeolite/poly(amino acid) composites with hemostatic activity for bone substitute applications

Biological Efficacy of Modified Structure of Polymer Surfaces for Bone Substitute

A novel strategy for calcium magnesium phosphate/carboxymethyl chitosan composite bone cements with enhanced physicochemical properties, excellent cytocompatibility and osteogenic differentiation

The preparation and application of calcium phosphate biomedical composites in filling of weight-bearing bone defects

Degradation of bone repairing composite of calcium polyphosphate fiber, calcium phospate cement and micromorselized bone in vitro

Study of the Mechanical Property of Magnetite/ Hydroxyapatite/ Chitosan Nano-Composite

Stereocomplexation Reinforced High Strength Poly(L-lactide)/Nanohydroxyapatite Composites for Potential Bone Repair Applications

High-strength porous polyetheretherketone/hydroxyapatite composite for the treatment of bone defect

Preparation, characterization and properties of nano-hydroxyapatite/polypropylene carbonate biocomposite

Mineralization, degradation and osteogenic property of polylactide multicomponent porous composites for bone repair: In vitro and in vivo study

Polyacrylic acid-reinforced organic-inorganic composite bone adhesives with enhanced mechanical properties and controlled degradability

Effects of bovine cancellous bone powder/poly amino acid composites on cellular behaviors and osteogenic performances

α-hemihydrate calcium sulfate/octacalcium phosphate combined with sodium hyaluronate promotes bone marrow-derived mesenchymal stem cell osteogenesis in vitro and in vivo

Preparation, characterization and cytocompatibility of porous ACP/PLLA composites.

Amorphous calcium magnesium phosphate nanocomposites with superior osteogenic activity for bone regeneration

Structure, properties and animal study of a calcium phosphate/calcium sulfate composite cement

Preparation and characterization of biodegradable chitosan/hydroxyapatite nanocomposite rods via in situ hybridization: a potential material as internal fixation of bone fracture