Mesoporous Amorphous Feooh-Encapsulated Bio2-X Photocatalyst with Harnessing Broad Spectrum Toward Activation of Persulfate for Tetracycline Degradation
Pengfei Wu,Zhaolong Liu,Li Wu,Yingkun Zhang,Bing Wang,Zhanghao Cheng,Wenquan Cui,Xiangyang Lv,Qingling Liu
DOI: https://doi.org/10.1016/j.cjche.2024.03.027
IF: 3.8
2024-01-01
Chinese Journal of Chemical Engineering
Abstract:With the growing concern about the water environment, the advanced oxidation process of persulfate activation assisted by photocatalysis has attracted considerable attention to decompose dissolved organic micropollutants. In this work, to overcome the drawbacks of the photocatalytic activity reduction caused by the photo-corrosion of non-stoichiometric BiO2–x, a novel material with amorphous FeOOH in situ grown on layered BiO2–x to form a core-shell structure similar to popcorn chicken-like morphology was produced in two simple and environmentally beneficial steps. Through a series of degradation activity tests of hybrid materials under different conditions, the as-prepared materials exhibited remarkable degradation activity and stability toward tetracycline in the FeOOH@BiO2–x/Vis/PS system due to the synergism of photocatalysis and persulfate activation. The results of XRD, SEM, TEM, XPS, FTIR and BET show that the loading of FeOOH increases the specific surface area and active sites appreciably; the heterogeneous structure formed by FeOOH and BiO2–x is more favorable to the effective separation of photogenerated carriers. The optimal degradation conditions were at a catalyst addition of 0.7 g·L–1, a persulfate concentration of 1.0 g·L–1, and an initial pH of 4.5, at which the degradation rate could reach 94.7% after 90 min. The influence of typical inorganic anions on degradation was also examined. ESR studies and radical quenching experiments revealed that ⋅OH, S O4−⋅, and ⋅ O2− were the principal active species generated during the degradation of tetracycline. The results of the 1,10-phenanthroline approach proved that the effect of dissolved iron ions on the tetracycline degradation was limited, and the interfacial reaction that occurs on the active sites on the material's surface was a critical factor. This work provides a novel method for the producing of efficient broad-spectrum Bismuth-based composite photocatalysts and photocatalytic activated persulfate synergistic degradation of tetracycline.