Enhanced effect of phenyl silane-modified hexagonal boron nitride nanosheets on the corrosion protection behavior of poly(arylene ether nitrile) coating

Yunqing Xia,Shuai Zhang,Lifen Tong,Guo Lin,Zhongxiang Bai,Xiaobo Liu

DOI: https://doi.org/10.1016/j.colsurfa.2022.129869

2022-11-05

Abstract:Developing alternative protective coating with long serve life under complicated aggressive condition possesses desperate need in corrosion protection filed. Herein, a high performance functional polymer called poly(arylene ether nitrile) (PEN) was employed as a novel organic corrosion protection coating for preservation of P110 steel in this work. The phenyl silane functionalized hexagonal boron nitride (h-BN-MPDTS) synthesized via silylation reaction was introduced into PEN, forming a more efficient protection coating system with superior corrosion resistance. The obtained EIS experimental consequences confirmed that impedance of h-BN-MPDTS PEN coating (1.036 × 108 Ω cm2) was promoted by two orders of magnitude when compared to the neat coating (2.226 × 106 Ω cm2) with one time constant remained throughout the immersion process of 80 days. Meantime, less rust was seen from the artificial scratches of h-BN-MPDTS sample during the salt spray experiment, further demonstrating better corrosion resistance of h-BN-MPDTS PEN coating. Thus, this study provides a neoteric feasibility of high-performance polymer in anticorrosion coatings field.

chemistry, physical