Abstract:In this study, the rotating welding process of Chinese fir (Keteleeriafortunei) in Guizhou, China, was systematically analyzed. The effects of rotating welding conditions, including the dowel-to-guide hole diameter ratio, welding time, depth, base surface, angle, and dowel type, on the performance of welded Chinese fir were explored. Moreover, the physical and chemical changes oftheChinese fir interface during welding were revealed by Fourier-Transform Infrared Spectroscopy (FT-IR), X-ray Photoelectron Spectroscopy (XPS), X-ray Diffraction (XRD), and Scanning Electron Microscopy (SEM). The results indicated the following: (1) The rotating welding technology can quickly achieve a strong connection between wood through friction heat without chemical adhesives and compared with traditional wood connection technology such as gluing or mechanical fixing;it has the advantages of simple operation, high production efficiency; and environmental friendliness. (2) Aftertherotating welding, the wood underwent significant pyrolysis, especially the degradation of hemicellulose. The heat generated in the welding process caused good melting and mechanical interlocking between the dowel and the wall of the guide hole, but it was also accompanied by afriction loss of the dowel and the substrate. (3) The welding parameters affected the wood's connection strength and stability by altering heat production, distribution, transfer, and frictional losses. The impact of the dowel-to-guide hole diameter ratio had a great influence on the connection strength. When the diameter ratio was 1:0.7, the tensile strength was the highest, reaching 2.27 MPa. (4) The analyses of XPS, FTIR, XRD, and SEM proved thatthechemical composition changes at the interface, leading to a more structured crystalline bond and enhanced connection strength due to fiber entanglement and interlocking. This research providesatheoretical and experimental basis forthefurther innovation and development of wood processing technology and provides a new technical path forthegreen manufacturing of wood structure buildings.

Pullout Resistance of Densified Wood Dowel Welded by Rotation Friction

Pull-Out Performance of Densified Wood Dowels Embedded into Glued Laminated Timber

Experimental Research on Dowelled Connection of GluBam-Concrete Composite Beams

Wood dowel bonding by high-speed rotation welding

Axially Loaded Single Threaded Rod Glued in Glubam Joint

Effects of Dowel Rotation Welding Conditions on Connection Performance for Chinese Fir Dimension Lumbers

Tribological and Mechanical Properties of Wood Dowel Rotation Welding with Different Additives

Mechanical Behavior of Glued-in GFRP Rod in Glubam: Experimental and Analytical Study

Influence of the depth of friction-welded dowels on the strength of rotary welded joints

Experimental Study on Axial Pull-Out Behavior of Steel Rebars Glued-In Glubam

The Off-Axis Embedment Performance of Bamboo Panels Used for Glubam Structures

Pull-Out Behavior of CFRP Bars in Glued-In Glubam Joints

Strengthening of Composite T-joints Using Ø 0.11 Mm Z-pins Via an Ultrasound-Guided Insertion Process

Design Embedment Strength Of Plybamboo Panels Used For Glubam

Study on Pull-out Strength for Glued-in Rod Parallel to the Grain of Pinus Massoniana Lamb Glulam

Adhesive- and Metal-Free Assembly Techniques for Prefabricated Multi-Layer Engineered Wood Products: A Review on Wooden Connectors

Densified wood dowel reinforcement of timber perpendicular to the grain: a pilot study

Pull-out Strength for Glued-in Rod Parallel to the Grain of Structural Guled Laminated Bamboo

Characterisation of rotary friction welding process and mechanism of heat-treated Scotch pine

Experimental research on pull-out behavior of steel-UHPC composite beams with new composite dowels connectors

Bond Behavior Between Softwood Glulam and Epoxy Bonded-In Threaded Steel Rod