Secondary phase softening effect in PZT‐based ceramics by introducing the random electric fields

Feifei Guo,Qi Zhou,Yifei Chen,Chao Yang,Wenqiang Bai,Hongqiao Zhou,Ruigang Qiu,Wei Long,Pinyang Fang,Zengzhe Xi

DOI: https://doi.org/10.1111/jace.19160

IF: 4.186

2023-05-03

Journal of the American Ceramic Society

Abstract:In this work, the random electric fields are constructed in the hard PZT ceramics by adding the ZnO particles as a secondary phase to tune the piezoelectric properties and losses. It is found that the internal bias electric field existing in the hard PZT ceramics has been tuned successfully by the random electric fields and its value reduces with the increased ZnO content. As a consequence, the piezoelectric constant d33 reaches up to 483 pC/N in the PZT/0.75 wt%ZnO composite, which is much higher than that of the hard PZT matrix. In the meantime, the electromechanical quality factor Qm, dielectric loss tanδ and Curie temperature TC for this composite are about 1109, 0.55% and 279°C respectively. The promoted d33 is attributed to the small domain size and reduced internal bias electric field, while the low losses (large Qm and low tanδ) can be put down to the still existing non‐zero internal bias electric field. This article is protected by copyright. All rights reserved

materials science, ceramics